Catalytic conversion of 1,2-dichlorobenzene (1,2-DCBz) over V2O5/TiO2-based catalysts
Cuicui DU,Qiulin WANG,Shengyong LU,Jianhua YAN
DOI: https://doi.org/10.7524/j.issn.0254-6108.2017.01.2016052001
IF: 4.236
2017-01-01
Environmental Chemistry
Abstract:The effect of V primary oxidation state (V4+ or V5+) during the sol-gel preparation process on the catalyst after calcine was studied,and tests of its catalytic conversion activity on 1,2-dichlorobenzene (1,2-DCBz) was also conducted in a fixed-bed catalytic reactor,operating in a range of 150-350 ℃.Several physicochemical methods,including nitrogen adsorption,X-ray diffraction (XRD),X-ray photoelectron spectroscopy (XPS),H2 temperature programmed reduction (H2-TPR) and energy dispersive spectroscopy (EDS) were employed to characterize their structures and properties.Reducing V5+ of ammonium metavanadate to V4+ effectively improved the physicochemical ability of V2O5/TiO2,and thus promoted the catalytic conversion of 1,2-DCBz.The conversion efficiency of 1,2-DCBz increased from 43％ to 62％ over pre-reduced V2O5/TiO2 at 150 ℃.In the 220-350 ℃ range,over 10％ increase of 1,2-DCBz conversion was also obtained.This is ascribed to the mutual enhancement of adsorption and oxidation ability of the catalyst.Compared with V/Ti,the specific surface area and the total pore volume increased by 22 m2· g-1 and 0.09 cm3·g-1,respectively.The pores of 2-3 nn of pre-reduced V2O5/TiO2 also evidently increased.These results indicate the improvement of adsorption ability of the catalyst.Moreover,the raised average oxidation state of vanadium from 4.64 to 4.72 and concentration of surface active oxygen from 11％ to 13％ contributed to the enhancement of oxidation ability of pre-reduced V2O5/TiO2.However,Reducing V5+ of ammonium metavanadate to V4+ had less influence upon the V/Ti-CNTs catalyst.