Preparation and Characterization of Cellulose/Starch-based Biodegradable Plastic Film

ZHANG Rui-feng,HUANG Shao-bin,WU Wen-qing,ZHU Guang-fu
2012-01-01
Abstract:Using starch acetate(SA)and cellulose acetate(CA)dissolving in acetone,under the effect of tributyl citrate as crosslinking agent to conduct the crossed-Claisen condensation reaction,the biodegradable plastic film with different contents of starch-based material was prepared.The biodegradable plastic film was characterized by FT-IR,XRD,TGA and SEM.The results showed that SA dissolved well and had cross-linking reaction.Good performance biodegradable plastic film was prepared when the mass ratio of SA∶ CA=1∶ 1.With the increase of SA,the mechanical performance was declined,but the performance of degradation rate in the soil was better.In general,the biodegradable plastic film had good mechanical performances,thermal stability and easily degradable property.Take the plastic film when the mass ratio of SA∶ CA=1∶ 1 for example,its tensile strength can reach 11.13 MPa,elastic modulus can reach 214.29 MPa,the highest thermal stability temperature was 250 ℃,soil-burial degradation rate of 120 days can reach 50%.
What problem does this paper attempt to address?