Novel Conjugated Alternating Copolymer Based on 2,7-Carbazole and 2,1,3-Benzoselenadiazole
Wei Zhao,Wanzhu Cai,Ruixia Xu,Wei Yang,Xiong Gong,Hongbin Wu,Yong Cao
DOI: https://doi.org/10.1016/j.polymer.2010.04.057
IF: 4.6
2010-01-01
Polymer
Abstract:A novel conjugated alternating copolymer (PCzDBSe) based on N-9′-heptadecanyl-2,7-carbazole and 5,5-(4′,7′-di-2-thienyl-2′,1′,3′-benzoselenadiazole) was synthesized by Suzuki polycondensation. The polymer reveals excellent thermal stabilities with the decomposition temperature (5% weight loss) of 390°C and the glass-transition temperature of 140°C. The absorption peaks of the polymer are located at 412 and 626nm, respectively, while the absorption onset is extended to 716nm, which is 56nm red-shifted as compared with its analogue, poly[N-9′-heptadecanyl-2,7-carbazole-alt-5,5-(4′,7′-di-2-thienyl-2′,1′,3′-benzothiadiazole)] (PCDTBT). The HOMO and LUMO levels of the polymer were estimated to be −5.28 and −3.55eV, respectively, with an optical bandgap of 1.73eV. The hole mobility of PCzDBSe as deduced from a solution-processed organic field effect transistor (OFET) was found to be 3.9×10−4cm2V−1s−1. Polymer solar cells (PSCs) based on the blends of PCzDBSe and [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) with a weight ratio of 1:4 were fabricated. Under AM 1.5 (AM, air mass), 100mWcm−2 illumination, the devices were found to have an open-circuit (Voc) of 0.75V, a short-circuit current density (Jsc) of 7.23mAcm−2, a fill factor (FF) of 45% and a power conversion efficiency (PCE) of 2.58%. The primary results indicate that 5,5-(4′,7′-di-2-thienyl-2′,1′,3′-benzoselenadiazole) is a promising unit for low bandgap polymer for polymer solar cells.