Effects of lattice distortion on the electrical transport in Ca-deficient La0.67Ca0.33-xMnO3-δ (0≤x≤0.15) polycrystals
Shengming Zhou,Zhou Guien,Yuheng Zhang
DOI: https://doi.org/10.1016/S0921-4526(99)00878-9
2000-01-01
Abstract:Vacancies caused by Ca-deficiency in polycrystalline La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15) result in two obvious changes: one is a large increase of resistivity ρ in paramagnetic-insulator state; another is a decrease of Curie temperature T C . The conduction mechanism is of polaronic nature above T C , and the activation energy for the charge carries increases with increasing x . Rietveld refinement analyses show that the unit-cell volume V C shrinks abruptly accompanied by the insulator–metal transition and that the volume change of La 0.67 Ca 0.18 MnO 3− δ shows larger anomaly than that of La 0.67 Ca 0.33 MnO 3 around T C . Vacancies on A-sites introduce additional lattice distortions which can be partially removed below T C . Keywords La 0.67 Ca 0.33− x MnO 3− δ Insulator–metal transition Thermopower Volume thermal expansion 1 Introduction Recently, lattice distortion effects have been receiving much attention in the study of colossal magnetoresistance (CMR) materials such as La 1−x A x MnO 3 ( A = Ca,Sr,Ba or Pb) [1–12] . It was pointed out that double-exchange interaction between the Mn 4+ and Mn 3+ ions alone cannot account for many of the observed properties, and suggested that a strong electron–phonon coupling due in part to a Jahn–Teller (JT) splitting of the Mn e g states must be taken into account [1,2] . The presence of JT effects in these materials is expected to enhance polaron formation [1,2] . Increasing JT distortions is associated with increasing insulating behavior and decreasing T C , and such distortions can be partially removed below T C [1–4] . We assume that vacancies on A sites in La 1− x Ca x MnO 3 should lead to local distortions of MnO 6 octahedra and help to enhance polaron formation like JT distortion above T C . Doped LaMnO 3 system can tolerate a considerable proportion of vacancies on the A sites(La), giving rise to compositions such as La x MnO 3− δ [13–15] . This deficient perovskites are worth studying simply because there has been relatively little work reported in the literature on this system, and that such system may exhibit some features to help us further understand the physics of CMR materials. In this paper, the local lattice distortions are caused by vacancies on A-sites in polycrystalline La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15). As expected, we observed that such distortion effects are similar to JT distortions on electrical transport properties. Increasing vacancies on A-sites increases lattice distortions, lowers T C , enhances the resistivity. Furthermore, the local distortions resulting from the vacancies can be partially removed below T C . 2 Experiment The La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15) samples were prepared from stoichiometic amounts of La 2 O 3 , MnO 2 and CaCO 3 by standard solid-state reaction method under identical external condition. The mixtures were ground and pre-sintered in air at 1000–1360°C for three days with two intermediate grindings. The calcined materials were reground to fine powder and then pressed into discs. A final sintering was carried out at 1380°C in air for 20 h. The samples were then slowly cooled down to room temperature. X-ray powder diffraction (XRD) analyses were performed using a MXP18AHF X-ray diffractometer with a rotating anode operating at 40 kV and 100 mA in the temperature range 20–300 K. The Cu K α radiation was selected using a graphite monochromator. Structural parameters were refined by the Rietveld method, using the program of DBWS-9411 [16] . Electrical resistivity was measured by the standard four-probe method. The thermoelectric power measurements were performed in a cryostat working from 300 K down to liquid nitrogen temperature. 3 Results and discussion All the obtained samples La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15) were analyzed by means of XRD resulting in a single phase with a perovskite-like structure. All reflections could be indexed on the basis of the orthorhombic cell (i.e., a≠b≠c, α=β=γ=90 0 ) with space group symmetry Pnma, and their orthorhombic lattice constants were related to the perovskite subcell lattice parameter a p by a≈ 2 a p , b≈2a p and c≈ 2 a p . In the temperature range 20–300 K, no structure transition was observed for the samples La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15). The temperature-dependent resistivity at zero field for the four samples with x=0.0, 0.05, 0.10 and 0.15 is shown in Fig. 1 . Here, two striking features are noteworthy. First, the peak values of resistivity ρ p increase with increasing vacancy ratio on A site, while their residual resistivity remains very small. For instance, the peak values for x=0.00, 0.05, 0.10 and 0.15 are 21.6,51.4,96.5 and 209.0 mΩ cm , respectively, i.e. increase with increasing x . Second, the peak temperature (the metal–insulator transition temperture, which is about equal to T C for our samples) decreases as vacancy ratio increases. T C 's for x=0.00, 0.05, 0.10, 0.15 are ∼ 268 , ∼258, ∼255, and ∼247 K , respectively. Fig. 2 shows the temperature dependence of thermopower S of La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05 and 0.10). Curie temperature is reflected here by a jump in the thermopower. At temperatures far below T C , a relatively small thermopower is observed which is consistent with the characteristic of metallic conduction. Each sample shows a positive enhancement of S as the temperature is lowered to T C . In the temperature range T > T C , it has been demonstrated that the electrical conduction for La–Ca–Mn–O system can be described by ρ=AT exp (E ρ /K B T) as predicted by small polaron hopping conductivity [17,18] . By fitting the resistivity data we obtained the activation energy E ρ for the four samples, and E ρ for x=0.0, 0.05, 0.10 and 0.15 is about 91.8, 112.8, 120.6 and 125.7 meV, respectively. On the other hand, the activation energy E S , which was obtained by fitting the thermopower data according to the formula [19] S =− E S /( eT )+ S 0 above T C , is about 3.4, 7.4 and 10.3 meV for x=0.00, 0.05 and 0.10, respectively. The difference between the activation energies for resistivity ρ and thermopower S is very large, and this confirms that the electrical conduction above T C in the Ca-deficient samples is of polaron-dominated conduction [19] . It is clear that E ρ considerably increases with increasing vacancy ratio on A-site. The explanation for the increase of E ρ must include local lattice distortions caused by the introduced vacancies. The increasing vacancy ratio x on A-site enhances the local distortions of MnO 6 octahedra, followed by an increase of unit cell vacuum (see Fig. 3 (a)). These distortions can be thought of as introducing impurity scattering potential, lowering the mobility of carriers which tend to trap the carriers as small polarons above T C , and are directly reflected in the activation energy of the samples. The increase of the activation energy with increasing x implies that vacancies assist localization of polarons, consequently steeply increasing the resistivity above T C (see Figs. 1 and 3(b )). Double exchange model cannot give very large resistivity around T C , because the model neglects the polaronic nature of carriers and cannot reduce the carrier kinetic energy around T C . Here the introduced vacancies further demonstrate that the polaronic nature of carriers plays an important role in electrical transport and is key to understanding the large resistivity around T C . In order to further demonstrate the correlation between these electrical transport features and the local lattice distortions, we carried out the XRD measurements in the temperature range 20–300 K, and the Rietveld refinement results are shown in Fig. 4 . As temperature is lowered below T C , the unit-cell volume V C shrinks abruptly accompanied by the sharp change in ρ . For La 0.75 Ca 0.25 MnO 3 , a sharp volume anomaly was also observed at T C , and the volume behavior is due to a sudden decrease of MnO 6 distortions at T C with decreasing temperature [3,4] . For the present sample La 0.67 Ca 0.33− x MnO 3− δ , the volume behavior implying a readjustment of the internal structural parameters reveals that lattice distortions are abruptly removed to some extent when ferromagnetic spin ordering occurs. The partial removal of distortions will result in the release of the trapped carries and decrease the resistivity. On the other hand, we note in Fig. 4 that the change ratio Δ V C /V C =[V C (T)−V C (T=300 K )]/V C (T=300 K ) for La 0.67 Ca 0.18 MnO 3− δ is obviously larger than that for La 0.67 Ca 0.33 MnO 3 in the temperature range around T C , and that in the other temperature range the change ratio Δ V C / V C for the two samples is almost the same. These behaviors can help to understand two electrical transport phenomena of La 0.67 Ca 0.18 MnO 3− δ and La 0.67 Ca 0.33 MnO 3 as seen in Fig. 1 , i.e., the larger resistivity value around T C for La 0.67 Ca 0.18 MnO 3− δ is due to the larger lattice distortions caused by vacancies on A-sites, and the close residual resistivity value far below T C for the two samples is due to the fact that the additional distortions caused by vacancies in La 0.67 Ca 0.18 MnO 3− δ are partially removed when T→0 K . In addition, the cell volume V c is strongly related to T C . Fig. 3 (a) and (c) demonstrate that reducing V C increases T C . This seems to originate from the same physics as the coupling between external pressure and resistivity [20] and can be interpreted as follows: The decrease of the cell volume increases the relevant Mn–O–Mn orbital overlapping ( t ij ), thus leading to a broader bandwidth W for the itinerant e g electrons. It is known that the Curie temperature T C increases when the effective bandwidth W for the itinerant e g electrons broadens [1,2] . Therefore, decrease of V C enhances ferromagnetic coupling and the Curie temperature. 4 Conclusions Vacancies on A-sites of polycrystalline La 0.67 Ca 0.33−x MnO 3−δ (x=0.00, 0.05, 0.10 and 0.15) directly distort the MnO 6 octahedra. The distortions trap and localize the carries, lower the mobility of carriers, reduce T C . The distortions induced by the vacancies can be removed to some extent as ferromagnetic spin ordering occurs, and the additional localization of carries caused by vacancies seems to delocalize greatly as temperature decreases below T C . Acknowledgements This work was financially supported by the Foundation of the Academia Sinica and by the Education and Science Committee of Anhui Province, People's Republic of China. References [1] A.J. Millis P.B. Littlewood B.I. Shraiman Phys. Rev. Lett. 74 1995 5144 [2] A.J. Millis Boris I. Shraiman R. Mueller Phys. Rev. Lett. 77 1996 175 [3] P.G. Radaelli M. Marezio H.Y. Hwang S.-W. Cheong B. Batlogg Phys. Rev. B 54 1996 8992 [4] P.G. Radaelli D.E. Cox M. Marezio S.-W. Cheong P.E. Schiffer A.P. Ramirez Phys. Rev. Lett. 75 1995 4488 [5] C.H. Booth F. Bridges G.H. Kwei J.M. Lawrence A.L. Cornelius J.J. Neumeier Phys. Rev. Lett. 80 1998 853 [6] S.J.L. Billinge R.G. DiFrancesco G.H. Kwei J.J. Neumeier J.D. Thompson Phys. Rev. Lett. 77 1996 715 [7] T.A. Tyson J. Mustre de Leon S.D. Conradson A.R. Bishop J.J. Neumeier H. Röder Jun Zang Phys. Rev. B 53 1996 13985 [8] M.R. Ibarra J.M. De Teresa J. Blasco P.A. Algarabel C. Marquina J. Garcia J. Stankiewicz C. Ritter Phys. Rev. B 56 1997 8252 [9] H.Y. Hwang S.-W. Cheong P.G. Radaelli M. Marezio B. Batlogg Phys. Rev. Lett. 75 1995 914 [10] J. Fontcuberta B. Martı́nez A. Seffar S. Pinol J.L. Garcı́a-Munoz X. Obradors Phys. Rev. Lett. 76 1996 1122 [11] J. Aarts S. Freisem R. Hendrikx H.W. Zandbergen Appl. Phys. Lett. 72 1998 2975 [12] Q. Huang A. Santoro J.W. Lynn R.W. Erwin J.A. Borchers J.L. Peng K. Ghosh R.L. Greene Phys. Rev. B 58 1998 2684 [13] S. Sundar Manoharan Dhananjay Kumar M.S. Hegde K.M. Satyalakshmi V. Prasad S.V. Subramanyam J. Solid State. Chem. 117 1995 420 [14] A. Gupta T.R. McGuire P.R. Duncombe M. Rupp J.Z. Sun W.J. Gallagher Gang Xiao Appl. Phys. Lett. 67 1995 3494 [15] S. Pignard H. Vincent J.P. Sénateur K. Fröhlich J. Souc Appl. Phys. Lett. 73 1998 999 [16] R.A. Young A. Sakthivel T.S. Moss C.O. Paiva-Santos J. Appl. Crystallogr. 28 1995 366 [17] N. Mott, Electronic Processes in Non-Crystalline Materials, Clarendon, Oxford, 1971. [18] D.C. Worledge L. Mieville T.H. Geballe Phys. Rev. B 57 1998 15267 [19] M. Jaime M.B. Salamon M. Rubinstein R.E. Treece J.S. Horwitz D.B. Chrisey Phys. Rev. B 54 1996 11914 [20] J. Fontcuberta V. Laukhin X. Obradors Appl. Phys. Lett. 72 1998 2607