Hyper-Cross-Linked Polymers-Derived Porous Tubular Carbon Nanofibers@TiO 2 toward a Wide-Band and Lightweight Microwave Absorbent at a Low Loading Content
Shuai Kang,Shiya Qiao,Yutong Cao,Zuming Hu,Junrong Yu,Yan Wang,Jing Zhu
DOI: https://doi.org/10.1021/acsami.0c11839
2020-09-29
Abstract:An enormous challenge exists in the achievement of one-dimensional (1D) dielectric carbon composite high-performance microwave absorbents at a low filling ratio. Porous/core–shell dual microstructures have been considered as the potential candidate for designing remarkable microwave absorbers with strong absorption and wide band. Herein, novel multiple-structured tubular carbon <sub>2</sub> (<sub>2</sub>) hybrids were constructed via the sequential steps of hydrolysis and pyrolysis. The dielectric properties of the as-prepared composites can be tuned by adjusting the relative content of the TiO<sub>2</sub> shell and carbonaceous temperature to enhance the impedance matching behavior. Notably, the minimum reflection loss (RL<sub>min</sub>) value reaches up to −61.2 dB with an effective absorption bandwidth (EAB) of 3.2 GHz at 3 mm, and the EAB can cover 5.3 GHz with a thickness of merely 2 mm when 1.3 mL of tetrabutyl titanate (TBT) and 700 °C pyrolysis temperature are optimized, respectively. Delightedly, the mixing ratio is only 10 wt %, outperforming that of the most-related composites. The heterogeneous interfaces in TCNFs–TiO<sub>2</sub> are beneficial for the interfacial polarization relaxation. Besides, the hybrids are enriched with numerous pores to favor the lightweight absorbers. The desirable design in the microstructure can provide a promising route in wide-band and lightweight microwave absorbents.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11839?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11839</a>.FE-SEM images of TPNFs and <sub>2</sub> composites with different TiO<sub>2</sub> contents, N<sub>2</sub> adsorption–desorption isotherms, DFT pore-size distribution plots, and the pore parameters of TPNFs, TCNFs, and <sub>2</sub>, and <sub>2</sub> at diverse pyrolysis temperatures, electromagnetic parameters, loss angle, and RL of pristine TCNFs, electromagnetic parameters and loss angle of crystalline TiO<sub>2</sub>, magnetic parameters and magnetic loss of heterostructured <sub>2</sub> with different TiO<sub>2</sub> contents, magnetic parameters, magnetic loss, and dielectric loss of heterostructured <sub>2</sub> at the different carbonization temperatures, 3D representations and 2D contour RL of <sub>2</sub>-600 °C, <sub>2</sub>-650 °C, <sub>2</sub>-700 °C, and <sub>2</sub>-750 °C, RL curves and dependence of matching thickness (<i>t</i><sub>m</sub>) vs frequency (<i>f</i><sub>m</sub>) of <sub>2</sub> at the wavelength of λ/4, and impedance, attenuation constant (α), and Cole–Cole semicircles of <sub>2</sub> with the different TiO<sub>2</sub> contents and at the different pyrolysis temperatures (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11839/suppl_file/am0c11839_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology