Synthesis and Aggregation-enhanced Emission of Polymethacrylate with Pentaphenylpyrrole Side Group
Pei-pei Yang,Li-chao Dong,Yuan-yuan Li,Long-long Zhang,Jian-bing Shi,Jun-ge Zhi,Bin Tong,Yu-ping Dong
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17001
2017-01-01
Acta Polymerica Sinica
Abstract:Methacrylate monomer M-PPP, which is aggregation-enhanced emission (AEE) active and with a conjugated pentaphenylpyrrole side group, was designed and synthesized through palladium-catalyzed cyclization of arylamine and diaryl acetylene, Suzuki cross-coupling and esterification with EDCI as dehydrant. A series of homopolymers P-1, P-2, P-3 and copolymers CP41, CP21, CP11, CP12, CP14 were prepared by free radical polymerization of M-PPP and copolymerization of M-PPP with BMA. The molar ratio of M-PPP unit and BMA unit in copolymers CPs was calculated based on the chemical shift and integrations of their CH2 groups. The content of M-PPP units in the copolymers was lower than those in raw materials, mainly due to the low polymerization activity attributed to the bulky conjugated pentaphenylpyrrole side group. The monomer M-PPP, the polymers P-1, P-2, P-3 and the copolymers CP41, CP21, CP11 were of high thermal stability with their decomposition temperature above 300 degrees C, while the decomposition temperatures of CP12, CP14 decreased slightly because of the lower content of the conjugated pentaphenylpyrrole side group. Both the monomer M-PPP and the polymers exhibited obvious AEE feature in THF/H2O mixture. The fluorescence intensity of the polymers increased slowly when the water fraction (f(w)) was above 20%, and it increased faster when f(w) is above 80%. The relative fluorescence intensity (I/I-0) reached to a maximum at f(w) of 95%, mainly attributed to the aggregation of the conjugated luminogen pentaphenylpyrrole segment in the side-chain and the entanglement of the flexible polymer main chains in THF/H2O mixture, which could restrict the motion of pentaphenylpyrrole and intramolecular rotation of the benzene rings, leading to enhanced fluorescence emission. The fluorescence intensity of M-PPP decreased a little when f(w) was lower than 70%, then increased sharply, and the maximal I/I-0 was 3.9 at f(w) of 95%, which was higher than those of the polymers due to the lower content of conjugated pentaphenylpyrrole side group in the polymers. The copolymers CPs exhibited similar AEE behavior as the polymers P-1, P-2, P-3 in THF/H2O mixture, and they showed better AEE feature when increasing the content of the conjugated pentaphenylpyrrole side group. Furthermore, the copolymers CPs could " turn-on" to detect lysine selectively in THF/H2O mixture due to the interaction of BMA unit and lysine, and more sensitive fluorescence response was observed for CP14 due to the higher BMA side-chain content, which is known to have stronger interaction with lysine.