Effect of Ti on the Microstructure and Wear Behavior of a Selective Laser Melted Al-Cu-Mg-Si Alloy
Qingzheng Wang,Nan Kang,Mohamed El Mansori,Tianyu Yu,Mourad El Hadrouz,Xianghui Huang,Xin Lin
DOI: https://doi.org/10.1016/j.wear.2023.204790
IF: 4.695
2023-01-01
Wear
Abstract:The elimination of hot cracking and enhancement of wear resistance have important practical significance for wide application of high-strength Al-Cu-Mg-Si series aluminum alloys fabricated by selective laser melting (SLM). In the present work, Ti was introduced to refine the microstructure of the selective laser melted Al-Cu-Mg-Si alloy, whose effect on the densification, microstructure evolution and wear resistance was explored in detail. After adding 0.6 wt % Ti, the microstructure transformed from coarse columnar grains to a fine duplex microstructure consisting of equiaxed and columnar grains, while microhardness of the SLM processed Al-Cu-Mg-Si alloy was increased from 148.9 & PLUSMN; 1.5 HV to 159.3 & PLUSMN; 1.7 HV, respectively. The wear behavior was evaluated on a ball-on-flat tribometer by sliding against 100Cr6 steel at room temperature. With the addition of Ti, the wear rate of SLM processed Al-Cu-Mg-Si was decreased by 49.6% for the applied load of 10 N. The refined heterogeneous microstructure helps to achieve strength-ductility synergy of the Al-Cu-Mg-Si-Ti alloy, which provides superior resistance to indentation behavior and initiation of cracks. The wear mechanism of the Al-Cu-Mg-Si alloy under the applied load of 10 N is abrasive wear and delamination wear, which for the Al-Cu-Mg-Si-Ti alloy is abrasive wear with slight delamination wear.