Abstract:Polystyrene/layered double hydroxide (PS/LDH) nanocomposites were prepared by in situ suspension polymerization of styrene in the presence of LDH intercalated with 4,4'-azobis(4-cyanovaleric acid) (ACP) groups and ACP/4-vinylbenzene sulfonate ( VBS) composite groups, respectively. The morphological structure, thermal degradation behavior and rheological properties of PS/LDH nanocomposites were characterized by transmission electron microscopy (TEM) X-ray diffraction (XRD), tbermogravimetric analysis (TGA) and capillary rheometry. It was found that ACP groups could successfully intercalate into the gallery of LDH individually or combined with VBS groups through the ion-exchange reaction. It was evidenced by the XRD and TEM results that PS/LDH nanocomposites with higher exfoliation degree of LDH could be prepared by using of LDH intercalated with ACP/VBS composite groups. LDH nano-layers were dispersed in PS matrix after the melt-processing. This was caused by the improved intercalation polymerization due to the initiation of intercalated ACP initiator. The TGA data evidenced that the thermal degradation temperatures of PS/LDH nanocomposites increased as the weight fraction of LDH increased, i.e, the thermal degradation temperatures corresponding to 10% weight loss were improved 25.4 degrees C, 34.4 degrees C, 47.4 degrees C and 52.9 degrees C when 1% , 3%, 5% and 7% LDH was incorporated into PS, respectively. It was also found that the melt flow rate of PS/LDH nanocomposites decreased as the weight fraction of LDH increased.

Preparation and characterization of surfactant-free polystyrene/layered double hydroxide exfoliated nanocomposite via soap-free emulsion polymerization.

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

The preparation of an elastomer/silicate layer nanocompound with an exfoliated structure and a strong ionic interfacial interaction by utilizing an elastomer latex containing pyridine groups.

Synthesis and characterization of polystyrene/layered double-hydroxide nanocomposites viain situ emulsion and suspension polymerization

Synthesis and characterization of polystyrene/layered double-hydroxide nanocomposites via in situ emulsion and suspension polymerization

Preparation and Structure of Polystyrene/Montmorillonite Nanocomposite

Synthesis and Characterization of Exfoliated Polystyrene/znal Layered Double Hydroxide Nanocomposite Via Emulsion Polymerization.

Preparation and structure of poly(styrene-acrylonitrile)/montmorillonite nanocomposite

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Exfoliation of Layered Double Hydroxide in Polystyrene by In-Situ Atom Transfer Radical Polymerization Using Initiator-Modified Precursor

Structural characterisation and thermal properties of exfoliated polystyrene/ZnAl layered double hydroxide nanocomposites prepared via solution intercalation

PREPARATION AND CHARACTERIZATION OF POLYSTYRENE/LAYERED DOUBLE METAL HYDROXIDE NANOCOMPOSITES

Preparation of a Fluorocarbon Polymerizable Surfactant and Its Application in Emulsion Polymerization of Fluorine-Containing Acrylate

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Preparation of monodisperse polystyrene microspheres with different functional groups using soap-free emulsion polymerization

Synthesis of Branched Surfactant Via Ethoxylation of Oleic Acid Derivative and Its Surface Properties

Preparation of CaCO3/Polystyrene Inorganic/Organic Composite Nanoparticles

Preparation and characterization of polystyrene microspheres in the presence of β-cyclodextrin

Studies on Novel Surfactant-Free Polystyrene Nanoparticles Formed in Microphase Inversion

Formation, Stabilization & Application of Polymeric Nanoparticles

Preparation and Characterization of Affinity Polymer Basic Microspheres by Soap-Free Emulsion Polymerization