Abstract:Calcium polyphosphate (CPP) was added to hydroxyapatite (HA) to develop a novel biphasic calcium phosphate (BCP). The effects of varying CPP dosage on the sintering property, the mechanical strength, and the phase compositions of HA were investigated. Results showed that CPP reacted with HA and produced beta-calcium phosphate (beta-TCP) and H2O and that an excessive dosage of CPP (> 10 wt%) obtained a novel BCP of beta-TCP/amorphous-CPP, while a lesser dosage of CPP (< 10 wt%) obtained a traditional BCP (HA/beta-TCP). The porous beta-TCP/amorphous-CPP scaffolds (porosity of 66.7%, pore diameter of 150-450 mu m, and compressive strength of 6.70 +/- 1.5 MPa) were fabricated and their in vitro degradation results showed a significant improvement of degradation with the addition of CPP.

A Novel Biphasic Bone Scaffold: Beta-Calcium Phosphate And Amorphous Calcium Polyphosphate