Study on a New Silicone Marine Anti-fouling Coatings

史航,陈晓蕾,刘永利,王鲁民

DOI: https://doi.org/10.3969/j.issn.1009-4369.2008.06.002

2008-01-01

Abstract:The silicone resin marine anti-fouling coating was prepared by using NaPT as the marine anti-fouling agents and silicone resin as the basic material.The morphological structure of silicone resin coating was investigated under SEM,and its static water contact angle of the coatings was tested.The result proved that the static water contact angle of coatings did not change too much when NaPT was added.This indicated that NaPT molecules were entrapped inside the bulk of the polymer matrix rather than aggregating on the surface,with little effects on the low surface energy properties.The estimated cumulative NaPT was obtained by measuring the electrical conductivity of the solution by standard curve method.It was found that there was no sudden release happened.Anti-fouling nets were hung between net cases in the test maritime space according to GB/T 5370-1985,test methods for anti-fouling paints model in shallow water.Month by month observation on the type,quantity and the propagation of marine fouling organisms were recorded and compared with a blank sample at the same time.It was observed the area ratio of fishnet coated with anti-adhesion coating was lower significantly than the comparison sample,showing excellent anti-fouling properties;and not barnacles and other large attachment of fouling organisms was found as well on the anti-fouling coated nets.