Compressional and shear wave velocities of Fe2SiO4 spinel at high pressure and high temperature
Qiong Liu,Wei Liu,Matthew Whitaker,Liping Wang,Baosheng Li
DOI: https://doi.org/10.1080/08957950802296287
2008-01-01
High Pressure Research
Abstract:Ultrasonic interferometric measurements on polycrystalline Fe(2)SiO(4) spinel were conducted simultaneously with synchrotron X-ray diffraction and X-ray imaging up to 6.5GPa, 1073K. The compressional and shear wave velocity data and the volume data were fitted to the third-order finite strain equations to derive the bulk and shear modulus and their pressure and temperature derivatives. The fitting results are as follows: K(s0)=204.5(7)GPa, =73.6(3)GPa, K '(s)=4.3(3), G '=1.2(1), (partial derivative K(s)/partial derivative T)(p)=-0.027(2)GPa/K, and (partial derivative G/partial derivative T)p=-0.017(1)GPa/K. Comparison of our current results with previous data on (Mg,Fe)(2)SiO(4) spinel with different compositions suggests that the bulk modulus (K(s)) increases slightly with increasing iron content, while the shear modulus (G), in contrast, shows a dramatic decrease. However, the pressure and temperature derivatives of K(s) and G remain nearly constant from Mg(2)SiO(4) to Fe(2)SiO(4) spinel with average values of 4.2-4.4, 1.2-1.3, -0.024 GPa/K, and-0.016GPa/K for K ' s, G ', (partial derivative K(s)/partial derivative T)(p), and (partial derivative G/partial derivative T)(p), respectively. The proposed version of equations to describe the effects of iron on the elastic moduli of ringwoodite are: K(s)=184.7+18.0 X(Fe), and G=118.7-41.5X(Fe).