Substance Flow Analysis of Aluminium in China for 1991-2007(Ⅱ):Quantity Loss of Aluminium from a Perspective of Life Cycle and Its Policy Implications

CHEN Weiqiang,SHI Lei,QIAN Yi

2009-01-01

Abstract:A sustainable metals industry is essentially based on a closed loop of metals,which is as far as possible free of quantity and quality losses in the social economic system.Quantity losses of aluminium along its life cycle can further be classified into two main categories:1)the deposited loss which is either landfilled or deposited in residue/slag/waste ponds and may be re-exploited in the future,such as red mud from the Bayer process;2)the dissipated loss which either lose their metal properties or dissipates into the environment and therefore cannot be reused or recycled,such as corrosion and dissipative uses of aluminium.Under the stocks and flows framework,the authors estimated quantity losses of aluminium from a perspective of life cycle in China during 1991-2007.It was concluded that:1)Mining showed the highest fraction of the total aluminium quantity losses,indicating 75.8%,69.2%,33.4%,and 26.8%for 1991,1996,2001,and 2007,respectively.It also showed the greatest potential to reduce the losses at all life stages;2)Excluding losses from mining,the total quantity losses of aluminium in China during 1991-2007 increased year by year;3)because of the rapid expansion of alumina production capacity using the Bayer Process,the average loss rate of aluminium in alumina refining process at national level increased continuously after year 2003.This inevitably led to a great increase in aluminium quantity losses in this process;4)the dissipated losses increased year by year during 1991-2007,while their proportions to the total life cycle losses were found to generally range between 29%-36%after 2001;5)the life cycle total quantity losses of aluminium by producing a ton of primary aluminium decreased year by year during 1991-2007,showing 2.31 tons,1.70 tons,0.58 ton,and 0.50 ton for 1991,1996,2001,and 2007,respectively,among which there were 0.365 ton,0.37 ton,0.28 ton,and 0.20 ton metal losses,respectively.For reducing and even avoiding aluminium losses with the ultimate aim of promoting sustainable utilization of aluminium,some important strategies were also provided for the Chinese government and aluminium industry community as follows:1)to continuously decrease the loss rate of aluminium from each life stage of it;2)to reduce both quantity and quality losses of aluminium from the recycling chain in next several decades.