Effect of Network Polymerization on the Pressure-Induced Structural Changes in Sodium Aluminosilicate Glasses and Melts: 27 Al and 17 O Solid-State NMR Study
bjorn o mysen,yingwei fei,kenji mibe,george d cody,yoo soo yi,sung keun lee
DOI: https://doi.org/10.1021/jp206765s
2012-01-01
Abstract:Probing the pressure-induced structural changes and the extent of disorder in aluminosilicate glasses and melts at high pressure remains a challenge in modern physical and chemical sciences. With an aim of establishing a systematic relationship between pressure, composition, and glass structures, we report Al-27 and O-17 3QMAS NMR spectra for sodium aluminosilicate glasses [Na2O:Al(2)O3:SiO2 = 1.5:0.5:2n with n = 1 (NAS150520, X-SiO2 = 0.5), 2 (NAS150540, X-SiO2 = 0.67), and 3 (NAS150560, X-SiO2 = 0.75)] quenched from melts at pressures up to 8 GPa. We also explore the stability of the Al-[4]-O-Al-[4] cluster in the highly depolymerized, NAS150520, glass at high pressure. For given glass composition, the Al-[5,Al-6] peak intensity increases with increasing pressure. The population of Al-[5,Al-6] increases linearly with X-SiO2 from NAS150520 (X-SiO2 = 0.5) to NAS150560 glass (X-SiO2 = 0.75) at both 6 and 8 GPa. The [5,6]Al/X-SiO2 ratio also tends to increase with pressure, indicating a possible relationship between Al-[5,Al-6] fraction and X-SiO2 that depends on pressure. The effect of pressure on the network connectivity in the sodium aluminosilicate glasses is manifested in the increase in Si-[4]-O-Al-[5,Al-6] peak intensity and the decrease in the nonbridging oxygen (NBO) fraction with increasing pressure. The fraction of Si-[4]-O-Al-[5,Al-6] in NAS150520 is smaller than in NAS 150560. Taking into consideration the pressure-induced Al coordination transformation in the fully polymerized glass (albite, Na2O:Al2O3:SiO2= 1:1:6, NBO/T = O), the fraction of Al-[5,Al-6] at a given pressure varies nonlinearly with variations of NBO/T. Al-[5,Al-6] fraction at 8 GPa increases with decreasing degree of melt polymerization from similar to 8% for fully polymerized albite melt (NBO/T = 0) to similar to 37% for partially depolymerized melt (NAS150560, at NBO/T = 0.29). Then it gradually decreases to similar to 15% for NAS150520 with further increase in NBO/T of 0.67. This observed trend in the densification behavior at a given pressure indicates competing densification mechanisms involving steric hindrance vs changes of NBO fraction in the silicate melts. The NMR results also suggest that both NBO and BO, particularly Si-[4]-O-Si-[4], interact with Na+, and thus the Na+ distribution is likely to be homogeneous around both NBO and BO at high pressure without spatial segregation of silica-rich and alkali-rich domains for the glass compositions studied here. The presence of the Al-[4]-(OAl)-Al-[4] cluster is distinct in the NMR spectrum for NAS150520 glass at both 6 and 8 GPa. A new scheme of pressure-induced structural transitions in silicate melts involving Al-[4]-O-Al-[4] includes the formation of Al-[4]-O-Al-[4].