Effect of Minor Alloying on the Glass Forming Ability of U-Co Alloy
Huang Huogen,Ke Haibo,Liu Tianwei,Zhang Pengguo,Tang Xiane,Wang Yingmin
2018-01-01
Rare Metal Materials and Engineering
Abstract:Minor alloying is a useful approach for promoting glass forming ability (GFA) of metallic glasses. U-Co metallic glasses can be achieved in a wide amorphous composition range, but their GFAs are very poor. This study is aimed to increase the GFA in U-Co system by minor alloying. Sn, Si, Be, Cu, Pd, Y and Zr were selected as different-typed minor alloying elements in U69.2Co30.8 alloy. The glassy U69Co30M1: (M=Sn, Si, Be, Cu, Pd, Y, Zr) ribbon samples were prepared by melt-spinning with a copper roller, and their phase formation and thermodynamics were investigated by X-ray diffraction (XRD) and differential scanning calorimetry (DSC) techniques. The results indicate that Sn element significantly improves the GFA of U-Co alloy, Si displays the second improvement, Be and Cu are slightly effective while Pd, Y and Zr deteriorate the GFA. Based on the combination of the melting behavior change reflected by the DSC result, and the relationship between the GFA and the melting temperatures, electro-negativities, atomic sizes of M elements as well as mixing-enthalpies of M-C, the effect of the minor alloying on the GFA in U-Co system should be attributed to the variation of both metallic liquid stability and the crystallization driving force.