Abstract:Novel orange-red Sr2GdSbO6: Eu3+( x = 0, 0.05, 0.1, 0.2, 0.3, 0.4, 0.5 and 0.6) phosphors were successfully prepared by the traditional high-temperature solid-state method. The results of Rietveld re finement, energy dispersive spectroscopy (EDS) spectrum and elemental mapping demonstrate that Eu3+ successfully replaces the Gd3+ sites and distributes uniformly in the particles of phosphors. The luminescence properties of Sr2GdSbO6 :Eu3+ phosphors were investigated in detail. The emission spectra of the strongest emission peak is the D-5(0) -> F- 7(1) (593 nm) transition, which can emit orange-red light under 393 nm excitation. When the doping concentration of Eu3+ ions is x = 0.2, the luminescence intensity of the phosphors reaches the highest. The detailed mechanism of concentration quenching is attributed to dipole-dipole interaction. The thermal stability values of Sr2GdSbO6 :0.2Eu(3+) phosphors are 87%, 82% and 114% under 393, 467 and 527 nm excitations, respectively. The causes of the abnormal thermal quenching under 527 nm excitation were analyzed. Based on the abnormal thermal quenching under 527 nm excitation, the optical thermometry properties of Sr2GdSbO6 :0.2Eu(3+) phosphors were investigated by fluorescence intensity ratio (FIR) technique, and appreciable relative sensitivity was obtained. The results suggest that Sr2GdSbO6 :0.2Eu(3+) phosphors can be potentially applied to w-LEDs and optical thermometers. (c) 2023 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights are reserved, including those for text and data mining, AI training, and similar technologies.

The Reduction of Eu3+ in Srb6o10 Prepared in Air and the Luminescence of Srb6o10 : Eu

Luminescence and Energy Transfer of SrMgB6O11:Eu2+,Mn2+for White Light Emitting Diodes

The Reduction of Re3+ in Srb6o10 Prepared in Air and the Luminescence of Srb6o10 : Re2+ (re=eu, Sm, Tm)

Preparation of Sr1−xCaxYSi4N7:Eu2+solid Solutions and Their Luminescence Properties

The Reduction of Eu3+ to Eu2+ in BaMgSiO4∶Eu Prepared in Air and the Luminescence of BaMgSiO4∶Eu2+ Phosphor

Study on the reduction of Eu3+→Eu2+ in Sr4Al14O25: Eu prepared in air atmosphere

Reduction and Luminescence of Europium Ions in Glass Ceramics Containing Srf2 Nanocrystals

Luminescence Properties of Eu[sup 2+] Ions in Sr[sub 5](BO[sub 3])[sub 3]Cl

Luminescence Properties Of Eu2+ Ions In Sr-5(Bo3)(3)Cl

Luminescence Properties of Eu2+‐Doped Glass Ceramics Containing SrF2 Nanocrystals

XANES at Eu-L3 Edge and Valence of Europium in SrB4O7: Eu and BaB8O13: Eu

Luminescence Properties and Energy Transfer in SrLa2Sc2O7 Co-Doped with Bi3+/M (M = Eu3+, Mn4+, or Yb3+)

Origin of the Red Luminescence in Sr3Al2O6:Eu Phosphor—from the Synergetic Effects of Eu2+ and Eu3+

Luminescence Properties and Optical Sensing Behaviors of Sr2GdSbO6:Eu3+ Phosphors

The Reduction of Eu3+ to Eu2+ in Bamgal10o17:Eu and the Photoluminescence Properties of Bamgal10o17:Eu2+ Phosphor

A New Phosphor SrGdGa3 O7:Eu 3+ and Its Luminescent Properties

Luminescence Properties of Sr2ZnWO6:Eu3+ Phosphors

XANES and Luminescence of CaBPO{sub 5}:Eu, SrB{sub 4}o{sub 7}:Eu and Ba{sub 3}(po{sub 4}){sub 2}:Eu Prepared in Air[the XANES is Stated for X-ray Absorption Near-Edge Structure]

A study on the luminescence of different crystallographic sites for Sr2SiO4 : Eu2 + phosphors

An Investigation of the Luminescence and Hemocompatibility Properties of Eu3+ Doped SrS Synthesized Via Sol–Gel Route

XAFS at Eu–L3 edge and UV–VUV excited luminescence of europium doped strontium borophosphate prepared in air