Abstract:Polyaniline (PANI) particles were synthesized using aniline (AN), dodecyl benzene sulfonic acid (DBSA), and ammonium persulfate (APS). The particles were analyzed using scanning electron microscope (SEM), X‐ray diffraction (XRD), and fourier transform infrared spectroscopy (FTIR). A PANI/waterborne polyurethane composite material (PANI‐WPU) was obtained by combining it with polyethylene glycol (PEG600), diphenylmethane diisocyanate (MDI), dimethylol propionic acid (DMPA), N‐methyl pyrrolidone (NMP), and dibutyltin lauric acid (DBTDL). The structure was characterized by the FTIR spectrum. The mechanical characteristics of the coating film were evaluated with respect to the PANI content, as well as its water absorption, glossiness, electrochemical corrosion resistance, and acid and alkali resistance. The PANI/waterborne polyurethane film has a maximum tensile strength of 23 ±1 MPa, an elongation of 1012%, a pencil hardness of 5H, a flexibility of 2 mm, an impact resistance of 50 cm, the water absorption of 14.66%, and the glossiness of 99.9 ±0.1 at 60°. When the PANI content is 0.7%, the mechanical characteristics, glossiness, and anti‐corrosion performance of the composite film improve. The corrosion inhibition efficiency of the aqueous polyurethane coating film with PANI can reach 99.74%, as shown by the examination of electrochemical polarization curves and impedance spectra. The tinplate is coated with a 0.7% PANI‐WPU composite material and edge sealing. This coating provides excellent protection against acid and alkali resistance, as demonstrated by its ability to withstand immersion in 10% H2SO4 and 10% NaOH solution for 90 days without any paint peeling off.

Coating Fine Copper Powder with Polyaniline

A Catalytic Oxidation Approach to Coat Copper Powder with Polyaniline

Chemical Synthesis, Characterization and Thermal Analysis of Polyaniline/Copper Composite Powder

Preparation and Performance of Silver Coated Copper Powder

Preparation of compound powder of Nickel-coated copper with chemical plating process

Evaluation of synthesized polyaniline nanofibres as corrosion protection film coating on copper substrate by electrophoretic deposition

Anti-oxidation Technique of Conductive Ultrafine Copper Powder

Fabrication and performance of silver coated copper powder

Synthesis and Characterization of Silver-Coated Copper Powder Layer

Preparation of Polyaniline/Epoxy Composite and Its Anti- Corrosion Performance

Preparation and properties of silver-coated copper powder with Sn transition layer

Preparation and anti‐corrosion performance of nano Polyaniline/Polyurethane interpenetrating network composite coating

Preparation and anti-oxidisation resistance of silver-coated copper powders by cobalt-modified copper powders

Preparation of silver-coated copper powder and its oxidation resistance research

Photoinduced Ordered Growth of Copper-Doped Polyaniline Nanotubes: A Method to Improve the Catalytic Activity for C-N Coupling Reactions

Polyaniline Doped with Modified Gold Nanoparticles and Its Electrochemical Properties in Neutral Aqueous Solutionelectronic Supplementary Information (ESI) Available: TEM Images and Cyclic Voltammograms. See Http://Www.rsc.org/suppdata/cc/b3/b309646g/

Preparation and corrosion resistance of polyaniline and waterborne polyurethane composite coating film

A Facile and Efficient Route for Coating Polyaniline Onto Positively Charged Substrate

Polyaniline/Fe3O4 Nanoparticle Composite: Synthesis and Reaction Mechanism.

Modification of Cu Nanoparticles with A Disulfide for Polyimide Metallization

High Performance Organic Coatings of Polypyrrole Embedded with Manganese Iron Oxide Nanoparticles for Corrosion Protection of Conductive Copper Surface