Abstract:Doping Mn 2+ ions into cesium lead halide CsPbX 3 (X = Cl, Br, I) perovskite nanocrystals (PNCs) has been proven to be an effective strategy to reduce the Pb 2+ content. However, excessive Mn 2+ ions may form the Mn–Mn dimers in PNCs, leading to concentration quenching effects and low photoluminescence quantum yields (PLQYs). Herein, secondary metal ions (Ni 2+ , Cu 2+ , Zn 2+ ) were introduced to substitute Pb 2+ ions as co-doped (Mn, M):CsPbCl 3 PNCs (M = Ni, Cu, Zn), which were prepared by a facile method under ambient conditions, aiming for positively passivating the surface defects and improving the Mn 2+ emission. Also, to protect the co-doped (Mn, M):CsPbCl 3 PNCs from moisture damage, we performed silica encapsulation, which further passivated surface defects due to the effective hydrolysis of silane. The evolution of optical properties and stabilities of three series of (Mn, M):CsPbCl 3 PNCs was compared. The PLQYs of co-doped (Mn, M):CsPbCl 3 PNCs were larger than those of single-doped Mn: CsPbCl 3 PNCs, especially for (Mn, Ni):CsPbCl 3 and (Mn, Cu):CsPbCl 3 , which can reach nearly 30%. The PLQYs of (Mn, Ni):CsPbCl 3 and (Mn, Zn):CsPbCl 3 PNCs decreased dramatically during the encapsulation process, while the PLQY values of (Mn, Cu):CsPbCl 3 remained 30% even after the same treatment process. Consequently, the prototypes of white light-emitting devices (WLEDs) were successfully fabricated based on orange-red (Mn, Ni):CsPbCl 3 @SiO 2 and (Mn, Zn):CsPbCl 3 @SiO 2 composites. The synergetic effects of co-doping transition metal ions and silica-shell coating on improving optical properties and stabilities were investigated. It has potential for a wide range of applications in the field of solid-state light emission.

Growth and photoluminescence of CdS and CdS:Mn Nanoribbons

Photoluminescence and Photoconductivity Properties of Copper-Doped Cd1−xZnxS Nanoribbons

Influence of Mn Doping on the Microstructure and Optical Properties of CdS

Characteristics and Optical Properties of Cd1−xMnxS Nanorods Prepared Through Hydrothermal Route

Photoluminescence Properties of Single Cds Nanorods

Near-Field Detected Photoluminescence Spectra of Sds(0.65)Se(0.35) Nanoribbon at Room Temperature

Surface States Induced Photoluminescence from Mn2+ Doped CdS Nanoparticles

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Near-infrared Colloidal Manganese Doped Quantum Dots: Photoluminescence mechanism and Temperature Response

Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

Gallium Doped N-Type Znxcd1-Xs Nanoribbons: Synthesis and Photoconductivity Properties

Microstructures and Luminescence Behaviors of Mn2+ Doped ZnS Nanoparticle Clusters with Different Core/shell Assembled Orders

Mn Derived Growth of CsPbBr3 Nanoplatelets for Stable and Bright Orange Emission

Synthesis of high aspect ratio quantum-size CdS nanorods and their surface-dependent photoluminescence

Colloidal manganese doped ZnS nanoplatelets and their optical properties

Multicolored Luminescent CdS Nanocrystals

Enhanced Visible Photoelectrochemical Properties of Zno/Cds Core/Shell Nanorods and Their Correlation with Improved Optical Properties

Synergetic effects of the co-doping transition metal ions and the silica-shell coating for enhancing the photoluminescence and stability of Mn: CsPbCl 3 nanocrystals and their application

Synergetic effects of the co-doping transition metal ions and the silica-shell coating for enhancing the photoluminescence and stability of Mn: CsPbCl3 nanocrystals and their application

Extended photo-response of ZnO/CdS core/shell nanorods fabricated by hydrothermal reaction and pulsed laser deposition.

Optical Waveguide Behavior of Se-doped and Undoped CdS One-Dimensional Nanostructures Using Near-Field Optical Microscopy