Direct hydrogenation of Mg under the action of FeTi1.2 (amorphous) and mechanical driving force

P. Wang,A. M. Wang,H. F. Zhang,B. Z. Ding,Z. Q. Hu

DOI: https://doi.org/10.1023/A:1010983629802

2001-01-01

Journal of Materials Science Letters

Abstract:The composition of Mg and amorphous FeTi1.2 was accomplished in the initial stage of RBM. Then under the action of catalytic phase amorphous FeTi1.2 and mechanical driving force, hydride of Mg began to form. As shown in Fig. 2, the profile corresponding to MgH2 became visible for the sample ground for 1 h, and the one to γ -MgH2 for 5 h. MgH2 and γ -MgH2 formed were all nanocrystalline with the average grain size of about 10 nm. The reason for the formation of highpressure phase γ -MgH2 has been reported in the previous work [9]. During the course of RBM, other than a small amount of α-Fe separated out, amorphous FeTi1.2 remained phase stability. The above results imply the possible application of amorphous FeTi1.2 in the improvement of hydriding kinetics of Mg. To investigate the hydrogenation behavior of Mg and catalytic role of amorphous FeTi1.2 during the course of RBM, TGA was performed for the samples ground for different periods. It was found that the dehydriding reaction for all the samples started to occur around 540 K. Fig. 3 gives the relationship between the hydrogen content in the samples and milling time under the present experimental condition. The hydrogen content increased slowly in the initial 2 h, then rapidly during the period of 2 h to 4 h, and finally almost saturated, reaching up to 3.7 wt.%. After 7 h of milling, the unreacted Mg was detected by TGA and XRD analysis (Fig. 2), which implies the existence of dynamic hydrogenation equilibrium in the course of RBM. The catalytic role of amorphous FeTi1.2 in the hydrogenation of Mg was confirmed by the fact that after pure