Abstract:In order to optimize the intrinsic gettering (IG) process based on the rapid thermal processing (RTP) for nitrogen-doped Czochralski (NCZ) silicon wafer, the effects of RTP and the following nucleation anneal on oxygen precipitation in NCZ silicon and conventional CZ silicon wafers have been comparatively investigated. It was found that, for NCZ silicon, the RTP at enough high temperature (e.g., 1250 degrees C) was necessary for generation of high density of bulk microdefects (BMDs) in the subsequent anneals despite the nitrogen enhancement effect on oxygen precipitation. With enough high concentration of vacancies introduced by the RTP at 1250 degrees C, for the conventional CZ silicon wafer, the vacancy enhancement effect on the nucleation of oxygen precipitates was most significant at 800 degrees C; while for NCZ silicon wafer, the vacancies and nitrogen atoms coacted most remarkably to nucleate the oxygen precipitates during the ramping anneal from 800 to 1000 degrees C. It was further found that the doped nitrogen is superior to the vacancy to enhance the nucleation of oxygen precipitates at temperatures of 900-1000 degrees C. Moreover, in order to maximize the density of BMDs, the RTP-based IG process for NCZ silicon wafer should be different from that for the conventional CZ silicon wafer. (c) 2005 American Institute of Physics.

Internal gettering for germanium-doped Czochralski silicon: Treated by rapid-thermal-anneal based processing simulation

Rapid-thermal-anneal-based Internal Gettering for Germanium-Doped Czochralski Silicon

Investigation of Intrinsic Gettering for Germanium Doped Czochralski Silicon Wafer

Intrinsic Gettering in Germanium-Doped Czochralski Crystal Silicon Crystals

Internal Gettering of Copper Contamination in Czochralski Silicon

Germanium in Czochralski Silicon

Rapid-Thermal-Processing-Based Intrinsic Gettering For Nitrogen-Doped Czochralski Silicon

Intrinsic Gettering In Nitrogen Doped Czochralski Crystal Silicon

Denuded Zone Formation in Germanium Codoped Heavily Phosphorus-Doped Czochralski Silicon

Germanium Effect on Oxygen‐related Defects in Czochralski Silicon

Effect of Vacancies on Oxygen Precipitation in Germanium-Doped Czochralski Silicon

Crystal-originated Particles in Germanium-Doped Czochralski Silicon Crystal

Germanium Doping of Si Substrates for Improved Device Characteristics and Yield

High temperature nucleation of oxygen precipitates in Germanium-doped Czochralski silicon

Electron Irradiation Induced Defects In Germanium-Doped Czochralski Silicon Substrates And Diodes

On the Assumed Impact of Germanium Doping on Void Formation in Czochralski-Grown Silicon

Influence of Germanium Doping on the Mechanical Strength of Czochralski Silicon Wafers

Enhanced Formation of Thermal Donors in Germanium Doped Czochralski Silicon Pretreated by Rapid Thermal Annealing

Effect of Germanium Codoping on the Grown‐In Oxide Precipitates in Nitrogen‐Doped Czochralski Silicon

Characterization of a Czochralski Grown Silicon Crystal Doped with 1020 Cm‐3 Germanium

Defect Engineering In Silicon Used For Ultra Large-Scale Integrated Circuits