Abstract:In this work, N-butyl methacrylate (BMA)/N-vinyl-2-pyrrilidone (NVP) amphiphilic core-shell nanoparticles were successfully prepared via miniemulsion copolymerization, the emulsion was initiated by the redox initiation couple of cumene hydroperoxide (CHPO) and ferrous sulfate hydrate (FS). The synthetic waterborne polyurethane (WPU) was used as surfactant and hexadecane (HD) as co-stabilizer, respectively. FTIR and XPS were used to confirm the occurrence of copolymerization between two monomers. TEM and DLS were used to observe the particle morphology and determine the particle size and its polydispersity index (PDI). It was found that the core-shell poly(BMA-co-NVP) nanoparticles prepared via interfacial-initiated miniemulsion copolymerization (IMEP) had relatively small diameters (40–120 nm) and narrowly particle size distribution (0.066–0.243). Only about 2 wt% surfactants based on the solution was enough to prepare a stable miniemulsion. The results demonstrated that IMEP prompted the copolymerization of water-soluble NVP monomer with oil-soluble BMA monomer to form core-shell nanoparticles. The effects of surfactant and co-stabilizer affect on the miniemulsion copolymerization were discussed. All the results indicate that the fabrication amphiphilic core-shell nanoparticles via IMEP were successful. Then the poly(BMA-co-NVP)/NiS hybrid materials were fabricate via the reaction of NiSO4 and CH3CSNH2 on the copolymers surface under 60Co γ-irradiation at room temperature and ambient pressure. The hybrid materials were characterized by FESEM.

Fabrication of carbon black/crosslinked poly(vinyl pyrrolidone) core-shell nanoparticles stable in water

Preparation and Properties of Crosslinked Β-Cd Polymer/Fe3O4 Composite Nanoparctiles with Core-shell Structures

Poly(vinyl Alcohol)‐encapsulated Hydrophilic Carbon Black Nanoparticles Free from Aggregation

One-stage Preparation of PSt/PNVP Core/Shell Nanoparticles Via Interfacial-initiated Microemulsion Copolymerization

Fabrication of Amphiphilic Porous PDVB-PAA Janus Nanoparticles: Formation Mechanism, Simultaneous Loading and Regulated Release of Hydrophobic and Hydrophilic Cargos

Fabrication of PVA/CNT/Pd Functional Hybrid Nanocomposite with Assistance of Supercritical CO_2

PREPARATION OF POLY (SODIUM 4-STYRENESULFONATE) GRAFTED CARBON BLACK Via ULTRASONIC IRRADIATION INITIATED RADICAL POLYMERIZATION

Suspended Carbon Black Fluids Reinforcing and Toughening of Poly(Vinyl Alcohol) Composites

Polymer-encapsulated Hydrophilic Carbon Black Nanoparticles Free from Aggregation

Highly homogeneous and stable single-walled carbon nanotubes dispersion modified by polyvinylpyrrolidone and alkanolamine in water

A simple method to synthesize multifunctional silica nanocomposites, NPs@SiO2, using polyvinylpyrrolidone (PVP) as a mediator

Water Dispersible Carbon Black Prepared Through Ultrasonically Assisted Radical Polymerization

Preparation of Core–shell Carbon Black Nanoparticles and Their Crystallization-Induced Orientation

Synthesis of Hollow PVP/Ag Nanoparticle Composite Fibers via Electrospinning under a Dense CO2 Environment

Water Stable Colloidal PVP coated Spin Crossover Nanoparticles

Poly(BMA-co-NVP)/NiS Core-Shell Hybrid Materials Via Interfacial-initiated Miniemulsion Copolymerization and Gamma-Irradiation

Preparation and Properties of Hydrophilic Carbon Black-Natural Rubber Nanocomposites

Effect of Electrostatic Heterocoagulation of PVM/MA Grafted Carbon Black and Attapulgite Nanorods on Electrical and Mechanical Behaviors of Waterborne Polyurethane Nanocomposites

Preparation and Characterization of Poly(sodium 4-Styrenesulfonate)-decorated Hydrophilic Carbon Black by One-Step in Situ Ball Milling

Synthesis of Nanocolorants with Crosslinked Shell by Miniemulsion Polymerization Stabilized by Waterborne Polyurethane

Effect of Poly(sodium 4-Styrenesulfonate) Modified Carbon Black on the Dispersion and Properties of Waterborne Polyurethane Nanocomposites