Abstract:Nanocomposite Nd2Fe14B/alpha-Fe magnetic material was prepared by the mechanical milling and a subsequent crystallization vacuum annealing treatment with the as-cast alloy of Nd2Fe14B atomic ratio and alpha-Fe. The effects of milling and crystallization conditions on the microstructure and magnetic properties were investigated by X-ray diffractometer (XRD), differential scanning calorimetry (DSC), and transmission electron microscropy (TEM), respectively. It was found that the grain sizes of both the Nd2Fe14B and the alpha-Fe phases decreased drastically with increasing the milling time. After milling for 5 h, the as-milled material was comprised of alpha-Fe nanocomposite phases of about 10 nm in size and some amorphous phases, which could be turned into the Nd2Fe14B/alpha-Fe nanocomposite phases by the subsequent crystallization annealing treatment. High magnetic properties could be achieved by the optimization of crystallization treatment process. In the present study, the best magnetic properties determined by PPMS were B-r=1.06 T, H-ci=347 kA/m, and (BH)(m)=142 kJ/m(3), respectively, when the material was milled for 5 h, followed by an annealing treatment at 650 degrees C for 30 minutes.

Microstructure and magnetic properties of nanocomposite Nd2Fe14B/α-Fe permanent magnetic powder prepared by mechanical milling