Can Copper Nanostructures Sustain High-Quality Plasmons?
Vahagn Mkhitaryan,Katia March,Eric Nestor Tseng,Xiaoyan Li,Leonardo Scarabelli,Luis M. Liz-Marzán,Shih-Yun Chen,Luiz H. G. Tizei,Odile Stéphan,Jenn-Ming Song,Mathieu Kociak,F. Javier García de Abajo,Alexandre Gloter,Luis M. Liz-Marzán,Odile Stéphan,F. Javier García de Abajo
DOI: https://doi.org/10.1021/acs.nanolett.0c04667
IF: 10.8
2021-03-02
Nano Letters
Abstract:Silver, king among plasmonic materials, features low inelastic absorption in the visible-infrared (vis-IR) spectral region compared to other metals. In contrast, copper is commonly regarded as too lossy for actual applications. Here, we demonstrate vis-IR plasmons with quality factors >60 in long copper nanowires (NWs), as determined by electron energy-loss spectroscopy. We explain this result by noticing that most of the electromagnetic energy in these plasmons lies outside the metal, thus becoming less sensitive to inelastic absorption. Measurements for silver and copper NWs of different diameters allow us to elucidate the relative importance of radiative and nonradiative losses in plasmons spanning a wide spectral range down to <20 meV. Thermal population of such low-energy modes becomes significant and generates electron energy gains associated with plasmon absorption, rendering an experimental determination of the NW temperature. Copper is therefore emerging as an attractive, cheap, abundant material platform for high-quality plasmonics in elongated nanostructures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.nanolett.0c04667?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.nanolett.0c04667</a>.Sections S1–S4: Details on NW synthesis and sample preparation, electron microscopy and EELS, electromagnetic simulations, deconvolution of EELS instrumental broadening, retrieval of plasmon full-width at half-maximum, and additional figures. Figure S1: Comparison between measured and calculated EELS spectra. Figure S2: Selection of results from Figure 1d. Figure S3: Plasmon dispersion and propagation length in infinitely long Ag and Cu NWs of selected diameters. Figure S4: Plasmon propagation in representative planar metal surfaces. Figure S5: Composition and crystallography of Cu NWs. Figures S6–S8: Details of plasmon width determination. Figure S9: Finite-difference time-domain simulations of the spectral width and quality factor <i>Q</i> of Cu and Ag NWs. Figure S10: Phase of the plasmon reflection coefficient <i>r</i> at the ends of Cu and Ag NWs (<a class="ext-link" href="/doi/suppl/10.1021/acs.nanolett.0c04667/suppl_file/nl0c04667_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology