Abstract:The monometallic catalyst Pd/TiO2-SnO2 was prepared by impregnating Pd on the surface of a composite support of TiO2-SnO2,which was prepared by coprecipitation.The prepared sample was characterized by X-ray diffraction（XRD）,specific surface area analysis（BET） and transmission electron microscopy（TEM） as nano-sized particles with average size of 9.1 nm and specific surface area of 100.08 m2·g-1.The Pd and TiO2 were dispersed on the surface of the SnO2 support in one monolayer,resulting in an increase of catalytic active sites.The catalytic performance of the Pd /TiO2-SnO2 catalyst for reduction of nitrate was investigated under normal atmosphere,with formic acid used as reducing agent.The results showed that the catalytic activity of the Pd/TiO2-SnO2 was positively related to load ratio and initial formic acid concentration but fluctuated with the temperature over the range of 15~45℃.With the temperature increasing,the catalytic activity initially increased then decreased.Increasing the amount of catalyst accelerated the reaction rate.The selectivity of Pd/TiO2-SnO2 was positively related to catalyst amount,but negatively related to load ratio,initial formic acid concentration and temperature.Strategies for control of the catalytic reduction of nitrate based on the formic acid-Pd/TiO2-SnO2 system are as follows：① To maintain high catalytic selectivity,the catalyst amount should be more than 0.1 mg.② To restrain pH rise and keep higher catalytic activity and selectivity,the molar ratio of formic acid and nitrate should be higher than 4：1;otherwise,the nitrate cannot be completely converted.③ The temperature should be controlled at the range of 25~35 ℃,since higher temperature（45 ℃） will cause catalyst deactivation while lower temperature（ 25 ℃） will reduce the catalytic activity and extend the reaction time.The ammonium formed during the catalytic reduction of nitrate can be completely removed by a cation-exchange process.

Catalytic reduction of nitrite ions in drinking water over Pd–Cu/TiO2 bimetallic catalyst

Titania-Supported Pd–Cu Bimetallic Catalyst for the Reduction of Nitrite Ions in Drinking Water

Catalytic Hydrogenation of Nitrate Ions over Pd-Cu/ZSM-5 Catalyst

Catalytic Reduction of Nitrate Nitrogen by Nano-Sized Bimetallic Pd-Cu/SnO_2 Catalyst

Highly Active Pd-In/mesoporous Alumina Catalyst for Nitrate Reduction.

Nitrate Hydrogenation on Pd–Cu/TiO2 Catalyst Prepared by Photo-Deposition

Insight into the bimetallic structure sensibility of catalytic nitrate reduction over Pd-Cu nanocrystals

Enhanced electroreduction of low-concentration nitrate using a Cu-Pd bimetallic cathode system: Performance evaluation, mechanism analysis, and potential applications

Titania-supported Bimetallic Catalysts for Photocatalytic Reduction of Nitrate

Synergistically enhancing nitrate reduction into N2 in water by N-doped Pd–Cu biochar bimetallic single-atom electrocatalysis

Adsorption and Reduction of Nitrate in Water on Hydrotalcite-Supported Pd-Cu Catalyst

Catalytic efficiency of Pd/TiO_2-SnO_2 in reduction of nitrate and control of the reaction

Catalytic Reduction of Nitrate in Water over Pd-Cu/γ-Al2O3 Catalyst

Size-Dependent Hydrogenation Selectivity of Nitrate on Pd−Cu/TiO2 Catalysts

Performance and Mechanism of Chelating Resin (TP-207) Supported Pd/Cu Bimetallic Nanoparticles in Selective Reduction of Nitrate by Using ZVI (zero Valent Iron) As Reductant

Unexpected Selective Photocatalytic Reduction of Nitrite to Nitrogen on Silver-Doped Titanium Dioxide

Hydrotalcite-supported Pd-Cu Catalyst for Nitrate Adsorption and Reduction from Water

Nano-spatially confined Pd-Cu bimetals in porous N-doped carbon as an electrocatalyst for selective denitrification

Electrochemical nitrate reduction over bimetallic Pd–Sn nanocatalysts with tunable selectivity toward benign nitrogen

Photocatalytic nitrate reduction over Pt–Cu/TiO2 catalysts with benzene as hole scavenger

Catalytic Hydrogenation of Aqueous Nitrate over Pd−Cu/ZrO<sub>2</sub>Catalysts