Abstract:Lead-free (1 - x) BaTiO3-x(Na0.5Er0.5)TiO3 (0 <= x <= 0.15) ceramics were prepared by a solid state reaction method. Their structure and electric properties were analyzed. Rietveld refinements suggested that the ceramics crystallized in the tetragonal perovskite space group P4 mm at room temperature. With increasing x from 0 to 0.05, Na+/Er3+ co-substitution at Ba-site in BaTiO3 leads to the decrease of lattice parameters and unit cell volume. While minor secondary phase, Er2Ti2O7 and (TiO1.2)(0.787), appears at x = 0.10 or above. A great enhancement of piezoelectric properties and other electric parameters was obtained in this system by properly moderating the compositions. For example, in the ceramics with composition x = 0.05, a large piezoelectric coefficient d(33) (333pm/V), a high remnant polarization P-r (14.3 mu C/cm(2)), a good planar electromechanical coupling factor k(p) (0.391), a mechanical quality factor Q(m) (97.3), and a high Curie temperature (T-C = 134 degrees C) (higher than that of pure BaTiO3) were achieved. Our results show that (1 - x) BaTiO3-x(Na0.5Er0.5) TiO3 ceramics are a good candidate of lead-free piezoelectric materials. (C) 2014 AIP Publishing LLC.

Study of New Lead-free Piezoelectric Ceramics of (na1/2bi1/2) TiO3- (na1/2bi1/2)(sb1/2nb1/2) O3

Largely Enhanced Electromechanical Properties Of Batio3-(Na0.5er0.5)Tio3 Lead-Free Piezoelectric Ceramics

Effect of B-site Complex Ions Substitution on Dielectric and Piezoelectric Properties of BNT Lead-free Piezoelectric Ceramics

Study of Dielectric Properties of (na1/2bi1/2 ) TiO3- ( Na1/2Bi1/2 ) ( Zn2/3Nb2/3 ) O3 Lead-free Piezoelectric Ceramics

Preparation and electrical properties of the new lead-free (1 − <i>x</i>)Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>–<i>x</i>Ba(Ni<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub> piezoelectric ceramics

Preparation and electrical properties of the new lead-free (1 − x )Bi 0.5 Na 0.5 TiO 3 – x Ba(Ni 1/3 Nb 2/3 )O 3 piezoelectric ceramics

Effect of B-site Complex Ions Substitution on Dielectric Properties of Na_(1/2)Bi_(1/2)TiO_3 Lead-Free Piezoelectric Ceramics

Piezoelectric and Ferroelectric Properties of LiNbO3-Doped (Bi0.5Na0.5)TiO3-(Bi0.5Na0.5)TiO3-BaTiO3 Lead-Free Piezoelectric Ceramics

Piezoelectric and Ferroelectric Properties of LiNbO_3-Doped (Bi_(0.5)Na_(0.5))TiO_3- (Bi_(0.5)K_(0.5))TiO_3-BaTiO_3 Lead-Free Piezoelectric Ceramics

Dielectric and piezoelecrtic properties of lead-free (Na0.5Bi0.5)TiO3–NaNbO3 ceramics

Ferroelectric and Piezoelectric Properties of 0.82(bi0.5na0.5) TiO3-(0.18-x)BaTiO3-x(Bi0.5Na0.5)(Mn1/3Nb2/3)O3 Lead-Free Ceramics

STUDY ON THE PIEZOELECTRIC PROPERTIES PF (Na0.88K0.12)0.5Bi0.5TiO3 LEAD FREE PIEZOELECTRIC CERAMICS MIXED WITH CeO2 AND Sb2O3

Microstructure, Density, and Dielectric Properties of Lead-Free (K<sub>0.44</sub>Na<sub>0.52</sub>Li<sub>0.04</sub>)(Nb<sub>0.96?x</sub>Ta<sub>x</sub>Sb<sub>0.04</sub>)O<sub>3</sub> Piezoelectric Ceramics

Microstructure, Density, And Dielectric Properties Of Lead-Free (K0.44na0.52li0.04)(Nb0.96-Xtaxsb0.04)O-3 Piezoelectric Ceramics

ELECTRICAL AND MECHANICAL PROPERTIES OF (1-X)(bi1/2na1/2)0.900ba0.088sr0.012tio3-x(bi1/2k1/2)tio3lead-free PIEZOELECTRIC CERAMICS

Study on the Dielectric Behavior of Bi(Mg2/3Nb1/3)O3 Doped Na1/2Bi1/2TiO3 Piezoelectric Ceramics

Synthesis and Piezoelectric Properties of Lead-Free (bi 0.5 Na 0.5 ) 1− X (ba a Sr B ) X TiO 3 Ceramics

Electrical Properties of Bi1/2Na1/2TiO3-BaTiO3 Ceramics Modified by BiFeO3

Effect of Substitution of Compensation Valence on Dielectric and Piezoelectric Properties of Lead-Free Piezoelectric Ceramics of (Bi_(1/2)na_(1/2))tio_3

Studies on [Bi_(0.5)(na_(1-X-y)k_xag_y)_(0.5)]_(1-z)ba_ztio_3 Lead-free Piezoelectric Ceramics

Piezoelectric and Dielectric Properties of (Bi0.5na0.5)0.94(ba1-Xsrx)0.06tio3 Lead-Free Piezoelectric Ceramics