Preparation and Properties of Uv-Cured Acrylated Silane Intercalated Polymer/Ldh Nanocomposite

Yan Yuan,Wenfang Shi

DOI: https://doi.org/10.1016/j.materresbull.2010.09.029

IF: 5.6

2011-01-01

Materials Research Bulletin

Abstract:A novel UV-cured polymer/layered double hydroxide (LDH) nanocomposite was prepared by modifying the LDH with sodium dodecyl sulfate (SDS) and [3-(methyl-acroloxy)propyl]trimethoxysilane (KH570) followed by UV irradiation after blended into a acrylate system. From the XRD analyses, the SDS-modified LDH-DS presented the basal spacing of 2.67nm, whereas the further KH570-intercalated LDH-KH showed a slight decrease to 2.41nm. After UV irradiated the exfoliated microstructure was formed, and observed by TEM and HR-TEM, showing the fine dispersion and random orientation of LDH in the polymer matrix. The storage modulus and glass transition temperature of the nanocomposite containing 5% LDH-KH increased to 47.5MPa and 67.8°C, respectively, from 39.7MPa and 66°C of the pure polymer from DMTA measurements. The tensile strength and Persoz hardness were enhanced to 10.6MPa and 111s, respectively, from 7.7MPa and 85s of the pure polymer.