Abstract:Visual summary of the article. Drilling glass fiber reinforced polymer matrix (GFRP) composites typically causes burrs, splintering, and microcracks within the GFRP structure, as well as delamination, fiber pull‐out, and thermal degradation of the polymer matrix. Designing and manufacturing molded‐hole GFRP components, as opposed to drilling, has recently been proposed as a promising method for overcoming the issues associated with drilling, for which there is limited research. Specifically, the mechanical response of molded‐hole GFRP has not been fully addressed in the literature. In the present study, molded and drilled GFRP composites with epoxy matrix were fabricated by hand lay‐up, and then the samples were analyzed utilizing experimental and numerical analysis techniques. Stress and strain analyses of GFRP samples were performed in Ansys Transient Structural Analysis. Although the fiber orientations of the layer geometries [0°/90°] and 3D models were the same, an additional layer was defined in the direction of the fiber orientation [45°/−45°] of molded‐hole composites to simulate the fiber accumulation effect. Experimental findings revealed that the flexural strength of molded composites was 12% greater than that of drilled composites. According to the numerical analysis, 98.7% proximity was achieved between the experimental and numerical results. Thus, the present study has provided numerical modeling to understand the flexural strength of molded composites for the first time, which will contribute to the increased use of molded composites in numerous applications in the fields of aerospace, automotive, and marine. Highlights Drilled‐ and molded‐hole GFRP composites were produced by hand lay‐up. Flexural properties of the composites were examined via 4P bending tests. Flexural strength of molded composites was higher than that of drilled ones. 98.7% proximity was achieved between the experimental and FEM results. A unified FEM method is proposed for the molded‐hole composites.

Tensile Strength and Fracture Behaviors of Complex GFRP Composites with a Central Hole

Tensile strength and fracture of glass fiber-reinforced plastic (GFRP) plate with an eccentrically located circular hole

Influence of Fiber Cutting at the Composite Grid Intersection on the Compressive Performance of Laminate

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Experimental Studies on Fracture of Unidirectional Glass-Fibre-Reinforced Plastics Composites with V-Notch

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Failure Mechanism of Tensile CFRP Composite Plates with Variable Hole Diameter

Tensile Behavior of Double-Hole CFRP Composite with Different Holes Position

Interlaminar Fracture Toughness Characterization of Laminated Composites: A Review

Impact of Holes on the Reduction of the Strength of Composite Specimens with Different Laying of Fibers

Enhanced Open-Hole Strength and Toughness of Sandwich Carbon-Kevlar Woven Composite Laminates

Experimental Determination of Fracture Toughness of Woven/Chopped Glass Fiber Hybrid Reinforced Thermoplastic Composite Laminates

An experimental and statistical evaluation of flexural performance of single and double notched glass/epoxy composite

Effect of Hole Arrangement on Failure Mechanism of Multiple-Hole Fiber Metal Laminate under On-Axis and Off-Axis Loading

Experimental investigation on the axial compression behaviour of perforated glass fibre reinforced plastic medium-length tubes

Investigation on Fracture Behavior of Glass Fiber Reinforced Thermoplstic and Thermosetting Composites

Damage characterization of FRP embedded with different optical fibers under tensile load using acoustic emission and micrographic real-time inspection

Experimental and numerical analysis of drilled‐ and molded‐hole glass fiber reinforced polymer matrix (GFRP) composites

Effect of fiber orientation on the failure behavior of a glass-fiber reinforced thermoplastic composite

Notch effect in tension-tension fatigue of short glass fibre reinforced polyphenylene sulfide composites

Evaluation and Comparison of Fracture Toughness of Glass Fibre Reinforce Composites