NaOH Solution Hydrothermal Growth and Superconducting Properties of BaPb1−xBixO3 Single Crystals

S HIRANO,S TAKAHASHI
DOI: https://doi.org/10.1016/0022-0248(87)90030-3
IF: 1.8
1987-01-01
Journal of Crystal Growth
Abstract:BaPb1−xBixO3 (BPB) single crystals were grown hydrothermally in a NaOH hydrothermal solution, in which the chemical composition of the grown crystals could be easily controlled over the range 0 ⩽ × ⩽ 1. the solibility increased with dissolution temperature and solvent concentration. The dissolution reaction obeyed Van't Hoff's law, indicating participation of hydroxide ions. The dissolution enthalphy was about 55 kJ/mol. single crystals 5×5×4 mm3 in size could be grown in Au capsules of 9.7 mm inner diameter at 100 MPa and 400°C. Single crystals of BaPb0.75Bi0.25O3 showed a sharp superconducting transition at 11.7 K with a ▿T of 1.6 K. The crystal structure was confirmed by X-ray crystallographic experiments to be tetragonal with a superlattice structure. The superconductivity of BPB may be responsible for the superlattice structure.
What problem does this paper attempt to address?