Abstract:Introduction: Bone defects remain a thorny challenge that clinicians have to face. At present, scaffolds prepared by 3D printing are increasingly used in the field of bone tissue repair. Polylactic acid (PLA) has good thermoplasticity, processability, biocompatibility, and biodegradability, but the PLA is brittle and has poor osteogenic performance. Beta-tricalcium phosphate (Î2-TCP) has good mechanical properties and osteogenic induction properties, which can make up for the drawbacks of PLA. Methods: In this study, photocurable biodegradable polylactic acid (bio-PLA) was utilized as the raw material to prepare PLA/Î2-TCP slurries with varying Î2-TCP contents (Î2-TCP dosage at 0%, 10%, 20%, 30%, 35% of the PLA dosage, respectively). The PLA/Î2-TCP scaffolds were fabricated using liquid crystal display (LCD) light-curing 3D printing technology. The characterization of the scaffolds was assessed, and the biological activity of the scaffold with the optimal compressive strength was evaluated. The biocompatibility of the scaffold was assessed through CCK-8 assays, hemocompatibility assay and live-dead staining experiments. The osteogenic differentiation capacity of the scaffold on MC3T3-E1 cells was evaluated through alizarin red staining, alkaline phosphatase (ALP) detection, immunofluorescence experiments, and RT-qPCR assays. Results: The prepared scaffold possesses a three-dimensional network structure, and with an increase in the quantity of Î2-TCP, more Î2-TCP particles adhere to the scaffold surface. The compressive strength of PLA/Î2-TCP scaffolds exhibits a trend of initial increase followed by decrease with an increasing amount of Î2-TCP, reaching a maximum value of 52.1Â MPa at a 10% Î2-TCP content. Degradation rate curve results indicate that with the passage of time, the degradation rate of the scaffold gradually increases, and the pH of the scaffold during degradation shows an alkaline tendency. Additionally, Live/dead staining and blood compatibility experiments suggest that the prepared PLA/Î2-TCP scaffold demonstrates excellent biocompatibility. CCK-8 experiments indicate that the PLA/Î2-TCP group promotes cell proliferation, and the prepared PLA/Î2-TCP scaffold exhibits a significant ability to enhance the osteogenic differentiation of MC3T3-E1 cells in vitro . Discussion: 3D printed LCD photocuring PLA/Î2-TCP scaffolds could improve surface bioactivity and lead to better osteogenesis, which may provide a unique strategy for developing bioactive implants in orthopedic applications.

Fabrication of calcium sulfate/PLLA composite for bone repair.

Biological Efficacy of Modified Structure of Polymer Surfaces for Bone Substitute

Fabrication and mechanical properties of PLLA/PCL/HA composites via a biomimetic, dip coating, and hot compression procedure

Preparation, characterization and cytocompatibility of porous ACP/PLLA composites.

Mineralization, degradation and osteogenic property of polylactide multicomponent porous composites for bone repair: In vitro and in vivo study

Stereocomplexation Reinforced High Strength Poly(L-lactide)/Nanohydroxyapatite Composites for Potential Bone Repair Applications

Preparation and Properties of Calcium Sulfate Dihydrate/beta-Tricalcium Phosphate/Polylactide Composite

Composites of poly(L-lactide-trimethylene carbonate-glycolide) and surface modified calcium carbonate whiskers as a potential bone substitute material

Composites of Poly(l‐lactide‐trimethylene Carbonate‐glycolide) and Surface Modified SBA‐15 As Bone Repair Material

Electrospun Nanofibrous Scaffolds of Poly (L-Lactic Acid)-Dicalcium Silicate Composite Via Ultrasonic-Aging Technique for Bone Regeneration.

Biosoluble ceramic fiber reinforced poly(L-lactic acid) bone scaffold: degradation and bioactivity

Porous and self-strengthened poly(ε-caprolactone)/calcium sulfate hemihydrate composite fibers for bone regeneration

Fabrication of Mineralized Polymeric Nanofibrous Composites for Bone Graft Materials

Customized Design 3D Printed PLGA/Calcium Sulfate Scaffold Enhances Mechanical and Biological Properties for Bone Regeneration

Structure and Properties of Chitosan Derivatives Modified Calcium Polyphosphate Scaffolds

Novel highly bioactive and biodegradable gypsum/calcium silicate composite bone cements: from physicochemical characteristics to in vivo aspects

Fabrication and Characterization of Composites Composed of a Bioresorbable Polyester Matrix and Surface Modified Calcium Carbonate Whisker for Bone Regeneration

Fabrication and properties of PLA/Î2-TCP scaffolds using liquid crystal display (LCD) photocuring 3D printing for bone tissue engineering

Phosphonic Acid Coupling Agent Modification of HAP Nanoparticles: Interfacial Effects in PLLA/HAP Bone Scaffold

Osteogenesis of Mineralized Collagen Bone Graft Modified by PLA and Calcium Sulfate Hemihydrate: in Vivo Study

Fabrication and Properties of Mineralized Collagen‐chitosan/hydroxyapatite Scaffolds