Abstract:Porosity is a major casting defect in alloys with large solidification intervals due to the disordered microstructure and broad mushy zones,which decreases badly the mechanical performance.Hence,finding ways to effectively reduce the porosity,further to optimize microstructure and mechanical per-formance is of great significance.In this regard,the Al-Cu-based alloys with large solidification intervals are continuously processed by coupling the travelling magnetic fields (TMF) with sequential solidifica-tion.Additionally,experiments combined with simulations are utilized to comprehensively analyze the mechanism of TMF on the reduction in porosity,including shrinkage porosity and gas porosity,from dif-ferent perspectives.Current findings determine that downward TMF can effectually optimize together the porosity,microstructure and performance,by inducing the strong long-range directional melt flows,stabilizing the mushy zones,and optimizing the feeding channels and exhaust paths,as well as increas-ing the driving force of degassing process.Eventually,downward TMF can increase the ultimate tensile strength,yield strength,elongation and hardness from 175.2 MPa,87.5 MPa,13.3 ％ and 80.2 kg mm-2 without TMF to 218.6 MPa,109.3 MPa,15.6 ％ and 95.5 kg mm-2,while reduce the total porosity from 0.95 ％ to 0.18 ％.However,Up-TMF exerts negative effects on the optimization of porosity,microstruc-ture and performance due to the opposite strong directional magnetic force and melt flows.Overall,our study provides an effective way to optimize together the porosity,microstructure and mechanical performance,and reveals their relationship,as well as details the relevant mechanisms of TMF on the porosity reduction from different perspectives.

Solidification and Remelting of Aluminum Though Alumina Preform under a Centrifugal Force Field

Solidification And Remelting Of Al Through Al2o3 Fibrous Preform Under Centrifugal Force

INFILTRATION AND SOLIDIFICATION/REMELTING OF MOLTEN ALUMINUM IN A CENTRIFUGAL FORCE FIELD

Molten Al Infiltration and Solidification/remelting in a Centrifugal Force Field

INFILTRATION OF MOLTEN ALUMINUM WITH TRANSIENT SOLIDIFICATION AND REMELTING IN CENTRIFUGAL CASTING PROCESSES

Centrifugal infiltration process of tubular porous preform by a Binary Alloy

Centrifugal Infiltration Process of Fibrous Tubular Preform by Al–Cu Alloy

Infiltration of Fibrous Preform by Al-Cu Alloy in a Centrifugal Force Field

Flow of Molten Aluminum in Porous Medium during Centrifugal Infiltration Casting Process

Infiltration of Molten Aluminum with Heat Transfer in Circular Pipe by Centrifugal Force

Effects of Operating Conditions on Infiltration of Molten Aluminum and Heat Transfer in a Centrifugal Force Field

Infiltration of molten aluminum and heat transfer in centrifugal casting processes

HEAT TRANSFER OF MOLTEN METAL INFILTRATE THROUGH SiC PREFORM IN CENTRIFUGAL FORCE FIELD

Investigation on the Kinetics of Infiltration of Liquid Aluminium into an Alumina Fibrous Preform

Formation of Liquid Pools Entrapped Within Solid Grains of Za27 Alloys During Partial Remelting

Remelting of Primary Solid in Rapid Solidification of Deeply Undercooled Alloy Melts

Multiphase Flow in Directional Solidification of Metal Matrix Particulate Composites

Microstructure Formation in Centrifugally Cast Al–Bi Alloys

Numerical Simulation on Fluid Flow, Heat and Mass Transfer in Solidification of Fe-C Alloys

Reducing Porosity and Optimizing Performance for Al-Cu-based Alloys with Large Solidification Intervals by Coupling Travelling Magnetic Fields with Sequential Solidification

Microstructure Evolution During Remelting of High Solid Fraction ZL101 Alloy