Water-retaining Agent of Zeolite/Carboxymethyl Cellulose Grafted Acrylamide
ZHANG Xiu-lan,LI Yin-huan,NIU Ming-gai,PEI Qiang,WANG Ya-nan
DOI: https://doi.org/10.3969/j.issn.1003-0972.2012.04.028
2012-01-01
Abstract:Using ammonium N,N-methylene-bisacrylamide and potassium sulfate as crosslinker and initiator respectively,a water retaining agent was prepared by graft polymerization of acrylamide on microcrystal cellulose in the presence of zeolite.The structure and interface of composites were characterized by FTIR.Parameters affecting water-adsorbing speed and water-retention capacity,such as the ratio of cellulose to monomer,the amount of zeolite,initiator and crosslinker,neutralization degree and the mass ratio of acrylic acid to acrylamide,have been investigated.The absorbency of the composite to tap water(434 g/g) and 0.9 %NaCl(71 g/g) could be obtained when the ratio of zeolite,carboxymethyl cellulose,initiator and crosslinker to the monomer mass were 20%,3%,0.7%,and 0.04%,the mass ratio of acrylic acid to acrylamide was 5,and the neutralization degree was 77 %,respectively.