Abstract:A novel strategy was applied in the synthesis of γ-Fe2O3 pillared bentonite (γ-Fe2O3-P-Bent) by intercalating Fe3+ into bentonite in the presence of the surfactant CTAB as an expanding agent and template agent. Then γ-Fe2O3-P-Bent catalyst was used as a heterogeneous catalyst for photo-Fenton degradation of organic contaminants. CTAB can promote the formation of crystalline γ-Fe2O3 in the process of calcination. In addition, the CTAB also significantly increased the surface area of the composites. Only the α-Fe2O3 pillared bentonite (α-Fe2O3-P-Bent) could be obtained under the same conditions without CTAB. The as-obtained composites were well characterized by various techniques to study their morphological, structural and magnetic properties. The specific surface area of the γ-Fe2O3-P-Bent catalyst increased from 29 to 117m2/g compared to bentonite. The saturated magnetization (Ms) values of γ-Fe2O3-P-Bent was 10emu/g. The effects of various reaction parameters such as H2O2 dosage, initial pH value, γ-Fe2O3-P-Bent dosage on the degradation of RhB were studied. Under the best conditions (0.2g/L of catalyst, 10mM of H2O2), the γ-Fe2O3-P-Bent catalyst displayed to possess superior degradation ability to Rhodamine B (RhB) comparing the results with the α-Fe2O3-P-Bent. The catalyst showed efficient for the degradation of other organic dyes as well. After five reaction cycles the catalyst still showed high photocatalytic activity (91%), which showed that the magnetic catalyst possessed very stable, highly reactive, and easy to separate by an external magnetic field. Hence, this facile and high efficiency method may be extended to fabricate other types of magnetic materials.

Heterogeneous UV-Fenton Catalytic Degradation of Dyestuff in Water with Hydroxyl-Fe Pillared Bentonite

Catalytic Degradation of Orange II by UV-Fenton with Hydroxyl-Fe-pillared Bentonite in Water

Photocatalytic Degradation of Orange II by Fe-containing Pillared Bentonites

Photocatalytic Degradation of Methyl Orange by Fe-containing Pillared Bentonites

Fe Pillared Bentonite and Photo-Catalytic Degradation of Dye-Orange Ⅱ

Fe2O3-Pillared Rectorite As an Efficient and Stable Fenton-Like Heterogeneous Catalyst for Photodegradation of Organic Contaminants

UV-Fenton discolouration and mineralization of Orange II over hydroxyl-Fe-pillared bentonite

Synthesis, Characterization and Photo Degradation Application for Dye-Rhodamine B of Nano-Iron Oxide/Bentonite

A Novel Strategy for Preparation of an Effective and Stable Heterogeneous Photo-Fenton Catalyst for the Degradation of Dye

Heterogeneous Fenton for Removal Rhodamine-B by Iron-bearing Attapulgite Granular Catalysts

Iron Pillared Vermiculite As a Heterogeneous Photo-Fenton Catalyst for Photocatalytic Degradation of Azo Dye Reactive Brilliant Orange X-GN

Comparative Study of Catalytic Activity of Different Fe-pillared Bentonites in the Presence of UV Light and H2O2

Ferrous-Oxalate-Modified Aramid Nanofibers Heterogeneous Fenton Catalyst for Methylene Blue Degradation.

Heterogeneous UV/Fenton Catalytic Degradation of Wastewater Containing Phenol with Fe-Cu-Mn-Y Catalyst.

Degradation of Dyes in Aqueous Solutions by the Fenton Process

Degradation of Rhodamine B in Wastewater by Iron-Loaded Attapulgite Particle Heterogeneous Fenton Catalyst

Efficient Removal of Dyes Using Heterogeneous Fenton Catalysts Based on Activated Carbon Fibers with Enhanced Activity

Preparation of Fenton Catalysts for Water Treatment

Iron(III)–Alginate Fiber Complex As a Highly Effective and Stable Heterogeneous Fenton Photocatalyst for Mineralization of Organic Dye

Efficient Degradation of High Concentration Azo-Dye Wastewater by Heterogeneous Fenton Process with Iron-Based Metal-Organic Framework