Elucidation of the capillarity-promoted sintering of silver nanoparticles produced by a spark ablation vapor source
Yu Zhang,Junyu He,Jin Tong,Haiqi Lai,Peilin Liang,Zhongwei Huang,Shiwo Ta,Tingyu Lin,Guannan Yang,Chengqiang Cui
DOI: https://doi.org/10.1016/j.apt.2023.103972
IF: 4.969
2023-04-01
Advanced Powder Technology
Abstract:Through the spark ablation method, high purity, spherical silver nanoparticles (Ag NPs) with a size of 5 ± 3 nm are prepared. A solvent-assisted sintering method is developed to modulate the sintering structure and properties of the as-prepared Ag NPs. The effects of the solvents terpineol, polyethylene glycol-200, 1,2-propanediol, and ethylene glycol are explored. The results show that treatment with ethylene glycol causes the shear strength of the sintered Ag NPs at 180, 220, 260, and 300 °C to significantly improve from 0, 3.7, 22.1, and 64.6 MPa to 37.1, 56.1, 76.6, and 93.1 MPa respectively. Additionally, the size and number of voids in the sintered structure are significantly reduced. From the perspective of the capillary pressure induced by the solvent during sintering, a correlation between low solvent wettability and small agglomerate size of the Ag NPs is revealed, which reasonably explains the structure and properties of the sintered Ag NPs that were treated with different solvents. The spark ablation and solvent-assisted sintering methods provide a new approach for the fabrication and structure–property design of metal NPs for electronic applications.
engineering, chemical