Effect of Temperature on the Dielectric Properties of Polybenzoxazine Blend Resin

Liu Zhihua,Yuan Qiaolong,Huang Farong

DOI: https://doi.org/10.3969/j.issn.1009-9239.2013.01.007

2013-01-01

Abstract:A p-aminophenyl propargyl ether(appe) was synthesized,and a propargyl based benzoxazine(P-appe) was prepared with the appe,phenol and paraformaldehyde by Mannich condensation reaction.A benzoxazine blend(PAF/P-appe) was prepared by blending the P-appe and phenol/aniline-based benzoxazine(PAF) in solution,and the processibility of the PAF and P-appe blend resin and the effect of temperature on the dielectric properties of the cured resin were studied.The results show that the viscosity of the blend resin is lower than 50 mPa.s with the processing window at 80～200 ℃.The activity energy of the blend resin in gel process is 102.1 kJ/mol,and the water absorption of the cured resin is lower than 0.44%.With the increase of temperature,the dielectric constant of the cured resin increases,the peak tand of the cured resin shifts to higher frequency,and the content of intramolecular hydrogen bonding(-OH...N) in the cured resin increases.