Abstract:Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant elements in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes <60 nm following consolidation via hot pressing at 585 °C. The very fine grain structure results in excellent mechanical properties, as evidenced by nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure while also strengthening the materials. Finally, intermetallic particles with sizes of hundreds of nanometers form in all systems. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.

Failure mode and dynamic behavior of nanophase iron under compression

An Engineering Route to Synthesize Stable Bulk Nanocrystalline Magnesium with an Average Grain Size of 20 Nm

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Compressive, Tensile, And Dynamic Behavior Of Nanophase Iron

Hot Deformation Behavior and Processing Map of the Nanocrystalline Pure Mg

Bulk Nanocrystalline High-Strength Magnesium Alloys Prepared Via Rotary Swaging

Nanophase And Ultrafine-Grained Powders Prepared By Mechanical Milling: Full Density Processing And Unusual Mechanical Behavior

Compression Behaviour of Bulk Nanocrystalline Ni-Fe

Effects of Hot Pressing Temperature and Annealing Temperature on Microstructure and Compressive Properties of a Bulk Nanocrystalline AZ61 Magnesium Alloy Contain Ti

Microstructure and thermal stability of nanocrystalline Mg-Gd-Y-Zr alloy processed by high pressure torsion

Mechanical Behaviors of Electrodeposited Bulk Nanocrystalline Metals and Alloys

Dynamic nano precipitation behavior of as-cast Mg-4Li-4Zn-Y alloy during high temperature deformation

Nanoscale Deformation of Multiaxially Forged Ultrafine-Grained Mg-2Zn-2Gd Alloy with High Strength-High Ductility Combination and Comparison with the Coarse-Grained Counterpart

Nanocrystallization and precipitation behavior evolution of AZ80 magnesium alloy during multi-directional compression

Nanocrystallization and hydriding properties of amorphous melt-spun Mg65Cu25Nd10 alloy

Compression Behavior of Nanocrystalline Nickel at 77 K

Comparative Studies of Constitutive Properties of Nanocrystalline and Bulk Iron During Compressive Deformation

Microstructure and Mechanical Behavior of As‐Cast, Extruded and Nanocrystalline Mg‐9Li‐3Al‐2.5Sr Alloy

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation

The preparation and mechanical properties of nano-magnesium alloy bulks