Abstract:In order to realize the utilization of coal-fired solid waste and captured carbon dioxide, the effects of ratio of solid waste, mineralized curing pressure and mineralized curing temperature on the compressive strength and carbon fixation rate of aerated concrete were studied, with the coal-based waste, coal ash and desulfurization gypsum as the main raw materials and slag as the supplementary cementitious material. The crystal phase structure and micro morphology under different mineralized curing conditions were analyzed by XRD and SEM, and the effect of different mineralized curing conditions on the pore structure of aerated concrete was studied by MIP. The experimental results show that the appropriate residual water/slag ratio is helpful to improve the CO 2 fixation rate and early compressive strength of aerated concrete. When the CO 2 curing pressure increases from 0.05 MPa to 1.00 MPa, the carbon fixation rate increases by 24.8%, and the compressive strength increases first and then decreases. When the curing pressure is 0.1 MPa, the maximum compressive strength is reached. With the CO 2 curing temperature rising from 25 ℃ to 105 ℃, the carbon fixation rate and compressive strength increases first and then decreases. The carbon fixation rate reaches maximum of 7.21% at 45 ℃, and the compressive strength reaches maximum of 3.53 MPa at 65 ℃. According to analysis of XRD and SEM, the major mineralized products are CaCO 3 , which mainly exist in the form of calcite and vaterite. Higher curing pressure（≥0.2 MPa） is likely to cause micro-cracks at the product interface. With the increase of curing temperature, the mineralized products and hydrated products appear simultaneously. According to MIP analysis, the influence of mineralized curing on the pores of aerated concrete can be divided into two aspects: on the one hand, CaCO 3 and other products with small particle size can fill the pores of 10-50 nm, on the other hand, reaction heat of mineralization and volumetric expansion of products can cause the increase of 30-60 μm pores. The microstructure can be optimized by increasing the curing temperature, which can make the distribution of pores more uniform.

Preparation of autoclaved wall materials from oil shale ash

Preparation process and performance study of desert sand autoclaved bricks

Effects of Red Mud on Workability and Mechanical Properties of Autoclaved Aerated Concrete (AAC)

Study on Preparation of Decarburized Fly Ash-phosphogypsum Autoclaved Brick

Preparation and Performance Study of Alkali-active Gypsum Mixture System

Experimental Study on Mechanical Properties of Soft Clay Stabilized by Industrial By-Products

Preparation of Autoclaved Aerated Concrete from Construction Waste

Production of lightweight aggregates from bauxite tailings for the internal curing of high-strength mortars

Preparation and Experimental Study on A New Type of Exterior Wall Putty

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Effect of Curing Age on Material Properties of Autoclaved Light-Weight Concrete Wallboard

Influence of Calcined Flue Gas Desulfurization Gypsum and Calcium Aluminate on the Strength and AFt Evolution of Fly Ash Blended Concrete under Steam Curing

Preparation of Medium–Low Strength Hemihydrate Gypsum from Phosphogypsum and Grey Correlation Evaluation of Autoclaving Energy Consumption

Experimental Study on the Interrelationship between the Moisture Content and Drying Shrinkage of Autoclaved Aerated Concrete Wallboard

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Effect of Pore Structure on Thermal Conductivity and Mechanical Properties of Autoclaved Aerated Concrete

Effect of curing conditions on the alkali-activated blends: Microstructure, performance and economic assessment

Study on formulation of aerated concrete by CO2 mineralization using coal ash

Effect of Potassium Feldspar Sodium-feldspar Composite Flux on The Sintering Performance of Fly Ash-coal Gangue-phosphogypsum Based Wall Insulation Materials

Effects of foam stabilizers on the properties and microstructure of autoclaved aerated concrete from iron tailings