Giant Dielectric Response with Reduced Loss in Ceramics with Nominal Composition of La1.5sr0.5nio4-Sio2
X. Q. Liu,G. Liu,P. P. Ma,G. J. Li,J. W. Wu,X. M. Chen
DOI: https://doi.org/10.1007/s10832-016-0041-2
2016-01-01
Journal of Electroceramics
Abstract:Structures and dielectric properties of La 1.5 Sr 0.5 NiO 4 ceramics with different contents of SiO 2 additives were investigated. The La 1.5 Sr 0.5 NiO 4 particles were dispersed into SiO 2 matrixes via a sol-gel process, while the homogeneous distribution was destroyed by the reaction between La 1.5 Sr 0.5 NiO 4 and SiO 2 during the sintering process, so the composite ceramics consisted of La 1.5 Sr 0.5 NiO 4 , La 9.33 Si 6 O 26 and NiO phases. The dielectric constants at room temperature varied slightly, while the dielectric losses could be suppressed with a moderate amount of SiO 2 additive. Temperature-independent giant dielectric constant with low loss was achieved in the ceramics with nominal composition of La 1.5 Sr 0.5 NiO 4 –0.80SiO 2 . Based on the analysis of impedance spectra, the giant dielectric response in the composite ceramics was attributed to the combination of the small polaronic hopping and Maxwell-Wagner effect.