Abstract:Raman spectra of the delafossite CuGa1-xCrxO2 (0 <= x <= 1) solid solution films have been measured in the temperature range from 80 to 823 K. Raman phonon modes are observed at 224 (A(g)), 328 (A(2u)), 396 (E-g), and 757 (A(1g)) cm(-1) for the CuGaO2 film, and phonon modes of the CuCrO2 film are around 211 (A(g)), 324 (A(2u)), 458 (E-g), and 712 (A(1g)) cm(-1), respectively. The A(1g) phonon mode has a distinct redshift with increasing Cr composition, which indicates that the interatomic potential becomes weaker between Cu and O atoms. Except Raman modes at the Brillouin zone center, the additional phonon modes in the spectral range of 500-670 cm(-1) were observed due to Raman selection rules being relaxed by the crystal defects. With increasing temperature, the A(1g) phonon mode undergoes a larger phonon softening but a smaller line broadening relative to that of the E-g phonon mode, which indicated the anisotropic behavior for the delafossite CuGa1-xCrxO2 films. The nonlinear temperature dependence of the phonon frequency and linewidth is an indication of nonharmonic lattice dynamics. The Raman shift and the linewidth of the E-g and A(1g) optical modes as a function of temperature were studied as an experimental evidence of the combined effect of lattice expansion and anharmonic phonon-phonon interaction. And the three-phonon anharmonic coupling plays the dominant role in the anharmonicity behavior. The phonon anharmonicity behavior of the CuGaO2 and CuCrO2 films is slightly different. The larger Gamma(0) is intrinsic for the A(1g) mode of the CuGa0.8Cr0.2O2 film due to the broadening by the crystalline defects, which perturb the translation symmetry of the harmonic crystal, making the momentum conservation rule for phonon scattering partially relaxed.

Phonon Characterization of Raman Spectra in High T C Superconductors Y 1- X Gd X Ba 2 Cu 3 O 7-Δ

Phonon Characterization Of Raman-Spectra In High T-C Superconductors Y1-Xgdxba2cu3o7-Delta

Raman and Infrared Spectra of High Tc Superconducting Systems YBa2Cu3−xCoxO7−δ

Phonon Natures in Raman Spectra of Y-Ba-Cu-O Compounds.

Study of Low Frequency Phonon Modes in YBCO System

SPECTROSCOPIC STUDY ON SU-PERCONDUCTOR YBA2CU3OX

Single-crystal Micro-Raman Spectroscopy of Phases in the Y-Ba-Cu-O Superconductor.

Raman spectroscopic study of an apparent phase transition at 234K in the high-Tc superconductor YBa2Cu3−xVxO7−y

Low Frequency Phonon Model in YxPr1−xBa2Cu3O7 System

Raman Scattering in Superconducting NdO1−xFxBiS2crystals

SUPERCONDUCTIVITY IN Y1-xCaxBa2Cu3-xMxO7-δ (m=fe, Ni) SYSTEMS

Structural and Spectroscopic Evidence for Stable Chemical Bonds and the Correlation with Hightcsuperconductivity

Antiferromagnetic Ordering in the High-Tc Superconductors (y1−xgdx) Ba2Cu3O7−y

Temperature-Dependent X-Ray-Diffraction Study of Lattice Vibrational Behavior in Bi-System Superconductor

Femtosecond Spectroscopy Studies On Yba2cu3o7-X And Prba2cu3o7-X Epitaxial Thin-Films

Positron lifetime spectrum of Y1-xCaxBa2Cu4O8 (x = 0 approx. 0.15) superconductors

Infra- to Ultra-Sound Studies of Lattice Instability and Carriers in High-Tccuprate Superconductors

Temperature Dependence of the Far-Infrared Reflectivity Spectrum of the High-Tc Superconductor YBa2Cu3O7-y.

Correlation between optical phonon softening and superconducting $T_c$ in YBa$_2$Cu$_3$O$_x$ within $d$-wave Eliashberg theory

Raman scattering measurements of phonon anharmonicity in the delafossite CuGa<sub>1-<i>x</i></sub>Cr<sub><i>x</i></sub>O<sub>2</sub> (0 <i>x</i> 1) films

Structural Properties and Superconductivity in the Y1−xPrxBaSrCu3O7−δ System