Synthesis and Performance of Novel Fluorine-Containing Epoxy Vinyl Ester Resin

仇伟,潘沛颐,李晓艳,李欣欣,韩哲文

DOI: https://doi.org/10.14133/j.cnki.1008-9357.2011.02.010

2011-01-01

Abstract:A novel fluorine-containing epoxy vinyl ester resin（F-EVER） was synthesized using fluorine-containing epoxy（F-EP）,acrylic acid（AA） and methacrylic acid（MAA） as monomer.The resin was modified by maleic acid（MA）,FT-IR spectra,TGA and mechanical properties.The corrosive resistance of the cured resin was also investigated.Results showed that the F-EVER had best performance when resin was synthesized under DMF as catalyst,molar ratio of carboxyl groups to epoxy groups was 0.9,molar ratio of F-EP to MA was more than 0.1,and the mass fraction of polymerization inhibitor was 0.03%.Furthermore,both thermal and corrosive resistance were promoted due to introduction of the element fluorine.