Abstract:Recently the preparation of biodegradable materials using proteins from wheat, soy and corn has been widely studied due to their excellent cohesive, viscoelastic and gas barrier properties. The present work mainly focuses on the influences of starch and moisture contents on the dynamic rhelolgical behavior and uniaxial extensional deformation of glycerol plasticized gluten-starch composites. Wheat gluten,wheat starch and glycerol, compounds with weight ratio of 21:0:9,18:3:9,15:6:9, and 12:9: 9, respectively, were prepared by using a three-roll mixer. The compounds were molded into rectangle- or dumbbell-shaped samples of 2 min in thickness and 6 min in width at room temperature. The dynamic behaviors of the mixtures were Investigated using an Advanced Rheometeric Expansion System (ARES) at 0. 1 % strain and 30 degrees C. The tensile test was performed on a universal testing machine with an extension rate of 20 min min(-1). The results showed that the dynamic storage modulus ( G') of the composite increased with increasing starch fraction. The plasticized gluten forms a crosslinking network at 80 degrees C due to chemical reaction. The results of temperature scan revealed a "rubber plateau" at temperatures above 100 degrees C. The starch gelatinization was not observed upon heating the composites. It indicates that moisture mainly exists in the glycerol-rich region, and the starch granules act as inert fillers. The dynamic frequency sweep shows that the composites exhibit gel-like behavior at 30 degrees C A marked "second plateau" appears in the low frequency region, which reveals strong physical interactions between the starch particles and the protein matrix. The interactions between polar groups in starch and protein both lead to the formation of a physical network additional to the chemical crosslinked protein network. The results of uniaxial extensional deformation tests show that the tensile strength and the elongation at break decrease with increasing the starch fraction in samples with 10 % moisture. On the other hand, opposite results were observed in the composites containing 20% and 25% moisture, which could be ascribed to the dilution and lubrication between the starch granule and the gluten network by moisture.

PROPERTIES OF THERMO-MOLDED GLUTEN/GLYCEROL/SILICA COMPOSITES

Influence of Glycerol Content on Properties of Wheat Gluten/Hydroxyethyl Cellulose Biocomposites

Preparation and Properties of Gluten/calcium Carbonate Composites

Green biocomposites from wheat gluten and hydroxyethyl cellulose: Processing and properties

Structure and Properties of Methylcellulose Microfiber Reinforced Wheat Gluten Based Green Composites

Preparation and Properties of Wheat Gluten/rice Protein Composites Plasticized with Glycerol

RHEOLOGICAL BEHAVIORS AND MECHANICAL PROPERTIES OF GLUTEN-STARCH-GLYCEROL COMPOSITES

Preparation and Properties of Wheat Gluten/Silica Composites

Preparation and properties of wheat gluten/methylcellulose binary blend film casting from aqueous ammonia: A comparison with compression molded composites

Structure And Properties Of Green Composites Based On Wheat Proteins: A Review

Improved Tensile Strength of Glycerol-Plasticized Gluten Bioplastic Containing Hydrophobic Liquids

Preparation and Properties of Cross-linked Gliadin/chitosan Films

Biopolymer Composites of Wheat Gluten with Silica and Alumina

A Comparison Study of Wheat Gluten Composites Filled with Dialdehyde Starch and Native Starch

Morphology and Mechanical Properties of Thermo-Molded Bioplastics Based on Glycerol-Plasticized Wheat Gliadins

Preparation and Properties of Thermo-Molded Bioplastics of Glutenin-Rich Fraction

Thermo-Molded Wheat Gluten Plastics Plasticized with Glycerol: Effect of Molding Temperature

Development of chopped glass fiber composites with difunctional benzoxazine and bio‐based phthalonitrile copolymer: A study of mechanical and thermomechanical properties

Influence of Methylcellulose on Properties of Wheat Gliadin Film Cast from Aqueous Ethanol

Mechanical Performance and Thermal Stability of Glass Fiber Reinforced Silica Aerogel Composites Based on Co-Precursor Method by Freeze Drying

STUDY ON TLCP/GF/PPESK COMPOSITES