Abstract:Nanocrystalline ZnO films were grown on silicon substrate by hydrothermal synthesis at 125 °C, using diethanolamine as additive. A powder containing ZnO spheres, with diameters between 100 to 200 nm and formed by aggregation of ZnO nanoparticles, was also obtained as a secondary reaction product. The samples were studied by scanning electron microscopy, X-ray diffraction and photoluminescence (PL) spectroscopy. The effects of the [diethanolamine]/[Zn2+] molar ratio on morphological, structural and optical properties were studied, as well as the effect of laser illumination (λ = 325 nm) and annealing treatment on photoluminescence properties. The film samples exhibited a compact columnar structure, with thickness between 180 to 210 nm, which were not strongly affected by the diethanolamine concentration. The X-ray diffraction patterns from the films evidenced preferred orientation along the c-axis of the ZnO wurzite structure; while the nanospheres did not show any preferential crystalline direction. The PL spectra from the films showed large initial UV emission and a weak defect band centered in the yellow. A PL evolution while the samples were UV illuminated was observed. The relaxation of metastable phases (formed during the low temperature growth) involving the creation of point defects, is suggested. The predominance of the yellow defect band before and after treatment points at oxygen vacancies as the possible point-defect candidate.

Shape Tuning of ZnO with Ammonium Molybdate and Their Morphology-Dependent Photoluminescence Properties

Synthesis of Zno Nanoparticles with Controlled Shapes, Sizes, Aggregations, and Surface Complex Compounds for Tuning or Switching the Photoluminescence

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Effect of solution concentration on surface morphology, optical properties and solar light response of ZnO thin films

Preparation of ZnO Particle with Novel Nut-Like Morphology by Ultrasonic Pretreatment and Its Luminescence Property

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Effect of the morphology on the optical properties of ZnO nanostructures

Preparation and Growth Mechanism of ZnO with Spindle Shape

Morphology Controlling and Optical Property of ZnO Prepared by Hydrothermal Method

Influence of Temperature on the Morphology and Luminescence of ZnO Micro and Nanostructures Prepared by CTAB-assisted Hydrothermal Method

Metastability effects on the photoluminescence of ZnO nano-micro structures grown at low temperature and influence of the precursors on their morphology and structure

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Effective Regulation of ZnO Surface Facets for Enhanced Photoluminescence Properties Assisted by Zinc Quaternary Ammonium Salts

Morphology-Controllable synthesis of ZnO nano-/Micro- Structures by a solvothermal process in ethanol solution

Temperature-Dependent Photoluminescence of Nanostructured ZnO

Synthesis and electromagnetic characteristics of ZnO micro-crystal with varying morphology

Control of ZnO Morhpology by Solution Route