Photoluminescence of Nano-MEH-PPV Arrays

KONG Fan,HUANG Gao-shan,YANG Yi-min,YANG Chang-zheng,WU Xing-long,BAO Xi-mao,YUAN Ren-kuan

DOI: https://doi.org/10.3321/j.issn:1000-7032.2005.06.019

2005-01-01

Chinese Journal of Luminescence

Abstract:Poly(p-phenylene vinylene)(PPV) and its derivatives have been investigated in electronics and photonics because of their excellent electronic and optical properties.It has been demonstrated that nanostructured PPVs are endowed with specialties for applications in new fields,such as wave-guiding and all-optical switching.(Using) porous anodic alumina with an ordered nanopore array as a template,the luminescent polymer MEH-PPV has been embedded into the nanopores as the template was immersed in MEH-PPV solution for 48 hours,then the template was taken out and washed with THF to drive out MEH-PPV chains on the surface of the(anodic) alumina template and then nano-MEH-PPV array was formed after the solvent volatilizes.It was demonstrated by analyzing of photoluminescence(PL) spectra that the optical properties of the nano-MEH-PPV array are obviously different from that of MEH-PPV film.It is also represented experimentally that the conformation of MEH-PPV in the nanopores of the anodic alumina is chain bunch.The number of MEH-PPV chains in the bunch depends on the concentration of the polymer solution for preparing the nano-MEH-PPV(array).As the(anodic alumina) template is immersed in MEH-PPV solution with higher concentration,more MEH-PPV chains move into the nanopores to form the bunch.Due to interchain interaction,the energy bands of the MEH-PPV bunch are widened to decrease its energy gap,and then the PL peak of the nano-MEH-PPV is red-shifted.The more the polymer chains of the bunch,the wider the energy bands of the bunch and the larger the red-shift of the PL peak of the polymer in the nanopores.So the optical properties of the nano-MEH-PPV array can be controlled by adjusting the concentration of the polymer solution for preparing the nano-MEH-PPV(array.) It is demonstrated by the PL spectra of the nano-MEH-PPV array annealed at different(temperatures) that the(relaxation) of MEH-PPV in the nanopores is limited and the nano-MEH-PPV shows highly thermal stabilities.