Abstract:Poly(3,4-ethylenedioxythiophene) (PEDOT), a common constituent material used in the preparation of electrochromic devices (ECDs) when doped with the polymer anion poly(styrenesulfonate) (PSS), can also be used to form an electrode layer. Patterned ECDs may thus be fabricated by conventional spin-coating. Due to high wastage and low productivity in spin coating, the demand for low-cost ECDs is difficult to meet. The alternative use of screen printing, however, results in a major challenge due to difficulty in achieving the necessary continuity of the applied print and of the subsequent film forming uniformity when using standard PEDOT:PSS dispersion alone. The film forming property of PEDOT:PSS is shown here to be improved by dispersing in a water methanol mix to form a novel PEDOT:PSS-solvent compound, which, when combined together with the high boiling solvent dimethyl sulfoxide (DMSO) and a thickening binder solution of polyvinyl alcohol (PVOH), allows screen printing to perform well. The sheet conductivity of the printed PEDOT:PSS compound film is then further increased by studying post-treatment using strong and weak organic acids, illustrated by comparing p-toluenesulfonic acid (tosylic acid (PTSA)) with glacial acetic acid (CH3COOH (HOAc)) or oxalic acid (OA), respectively, over a range of concentration. In this way, the optimal processing concentration of acid is accordingly obtained to minimize sheet resistance. Screen printed patterned ECDs, based on the post-treated PEDOT:PSS compound electrochromic and electrode films using the optimal acid concentrations, were printed including electrolyte layers, were evaluated. Performance of lateral versus vertical ECD build architecture in respect to chromatic aberration, working voltage, time response, ion mobility in electrolyte type (gel/solution), absorbance at color-switching, as well as mechanical stability during repeated bending, was assessed. The optima of chromatic aberration and absorbance at color-switching were found to coincide with minimal sheet resistance of the novel PEDOT:PSS compound films. Almost equivalent sheet resistance was obtained with both PTSA and HOAc, each at optimal treatment dosage, showing newly that the weak organic acid post-treatment provides an equivalent effect in comparison with strong organic acid if used at sufficient concentration. Furthermore, the electrochromic performance of the experimentally prepared ECDs was shown to be close to the level obtained from conventional indium-tin oxide (ITO)-based ECDs, and retained stable performance for color-switching after repeated bending of 1 000 times.

Tuning the Electrochromic Properties of Poly(alkyl-3,4-ethylenedioxyselenophenes) Having High Contrast Ratio and Coloration Efficiency

Synthesis and Electrochemical Properties of a Novel Poly(ether Sulfone) with Oligoaniline Pendants

Electrosynthesis of electrochromic polymers based on bis-(4-(N-carbazolyl)phenyl)-phenylphosphine oxide and 3,4-propylenedioxythiophene derivatives and studies of their applications in high contrast dual type electrochromic devices

Preparation of Multicolor Electrochromic Polymer Composite Film with Laminated Structure

Electrochemical And Optical Properties Of The Poly(3,4-Ethylenedioxythiophene) Film Electropolymerized In An Aqueous Sodium Dodecyl Sulfate And Lithium Tetrafluoroborate Medium

Electrochromic Polymers Based on 1,4-Bis((9H-carbazol-9-yl)methyl)benzene and 3,4-Ethylenedioxythiophene Derivatives as Promising Electrodes for Flexible Electrochromic Devices

Dithenylpyrrole Structure Bridged with Phenyl or Biphenyl Rings: Molecular Configuration and Electrochromic Properties

All-Solid-State Electrochromic Device Based on Nanocellulose/PANI/PEDOT Ternary Hybrid System for High Optical Contrast and Excellent Cycling Stability

Electrochromic Properties of Polymers/Copolymers Via Electrochemical Polymerization Based on Star-Shaped Thiophene Derivatives with Different Central Cores

Solvent-induced lengthened conjugated chains in electrochromic PEDOT for enhanced optical modulation

Improving the electrochromic properties of the composite films for electrochromic device

Enhanced Optical Contrast and Switching in Near‐Infrared Electrochromic Devices by Optimizing Conjugated Polymer Oligo(Ethylene Glycol) Sidechain Content and Gel Electrolyte Composition

Liquid crystalline PEDOT derivatives exhibiting reversible anisotropic electrochromism and linearly and circularly polarized dichroism

Comparing build architecture and electrolyte of ITO-free flexible patterned organic screen-printed ECDs based on a novel PEDOT:PSS compound film post-treated with strong and weak organic acids

A Flexible Electrochromic Device Based on PEDOT: PSS Working in Visible and Infrared Band

1,4-Bis((9H-Carbazol-9-yl)Methyl)Benzene-Containing Electrochromic Polymers as Potential Electrodes for High-Contrast Electrochromic Devices

High Fluorescent Ethyl Acrylate Modified Pedot-Menh2 with Enhanced Electrochromic Performance

The Effect of Oligo(Ethylene Oxide) Side Chains: A Strategy to Improve Contrast and Switching Speed in Electrochromic Polymers

Modulating the Electrochromic Performances of Transmissive and Reflective Devices Using N, N-Dimethyl Formamide Modified Poly(3,4-Ethylenedioxythiophene)/Poly(Styrene Sulfonate) Blend As Active Layers

Electrosynthesis and Characterization of Aminomethyl Functionalized PEDOT with Electrochromic Property

4-(Trifluoromethoxy)phenyl-Containing Polymers as Promising Anodic Materials for Electrochromic Devices