Abstract:Particle size and size distribution are two of the most vital parameters of nanomaterials since their physical properties as well as applications are highly dependent on these key factors. The objective of this work is to study the particle size and size distribution of gold nanoparticles (AuNPs), which were synthesized by a simple green synthesis in HAuCl4 and water-soluble chitosan solution (WSCS). Transmission electron microscope (TEM) and small-angle X-ray scattering (SAXS) techniques were carried out to determine the particle size, size distribution and polydispersity of AuNPs. The evidences from TEM and SAXS indicated that AuNPs can be formed in spherical shape with the size in the range of 10–30 nm. From TEM, the particle sizes of the AuNPs prepared in WSC, S at the concentration of 0.02 and 0.05 mg/mL containing 0.1 mM HAuCl4 were 20.5 ± 2.1 and 21.2 ± 1.8 nm, respectively. By increasing the concentration of HAuCl4 precursor up to 0.5 mM, AuNPs exhibited a slightly larger particle size (24.4 ± 2.2 nm). The particle size, size distribution and polydispersity of AuNPs observed by TEM and SAXS were in agreement. However, AuNPs sizes from SAXS were smaller than those from TEM because only the Au core of the AuNPs was detected by X-ray scattering. In addition, the chemical structure and specific surface plasmon resonance (SPR) absorption of AuNPs were well characterized by FTIR and UV-vis spectrophotometer. The FTIR results of AuNPs implied that the stabilization of AuNPs in the WSCS was due to electrostatic interaction and steric hindrance of C=O, C–O–C, –OH, –NH2 groups. By using WSCS at concentration 0.02 and 0.05 mg/mL, the SPR absorption bands were observed at 545 and 535 nm, respectively. The TEM and SAXS results of AuNPs in this study will provide an essential basis for synthesis of metallic nanoparticles for various applications in the future.

Fabrication of Gold Nanoparticles with Different Morphologies in HEPES Buffer

Fabrication Of Dendritic Gold Nanoparticles By Use Of An Ionic Polymer Template

Controlled Synthesis of Gold Nanospheres and Single Crystals in Hydrogel

Synthesis of gold nanoparticles by reduction of HAuCl 4 under UV irradiation

Synthesis of Monodisperse Gold Nanoparticles Stabilized by Gemini Surfactant in Reverse Micelles

Controlling the Formation of Au Nanoparticles Using Functionalized Molecular Buffer Layers

Preparation Of Gold Nanoparticles Protected With Polyelectrolyte

The Interconversion Between Gold Nanostars and Gold Nanodendrites Controlled Via Temperature and the Concentration of Sodium Dodecyl Sulfonate

Morphology Controllable Preparation of Gold Nanoplates Through an Eco-Friendly Wet-Chemical Route

Shape-Controlled Gold Nanoarchitectures: Synthesis, Superhydrophobicity, and Electrocatalytic Properties

Synthesis of Gold Nanomaterials with Different Morphologies

Controlled Fabrication of Decahedral Gold Nanostructures by a Thermal Approach

Control of the Self-Assembly Behaviors of Charged Gold Nanoparticles

Formation and optical properties of gold nanoparticles synthesized in the presence of double-hydrophilic block copolymers.

Hydrothermal Syntheses of Gold Nanocrystals: from Icosahedral to Its Truncated Form

Study on particle size and size distribution of gold nanoparticles by TEM and SAXS

Experiment and Theoretical Study of Poly(vinyl Pyrrolidone)-Controlled Gold Nanoparticles

Synthesis of Nanosized Gold Suspensions with Monodisperse Property

The High Yield Synthesis and Characterization of Gold Nanoparticles with Superior Stability and Their Catalytic Activity

Epoxy-Amine Microgels-Mediated Green Preparation of Gold Nanoparticles

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth