Abstract:Nanocomposite particles of amorphous carbon-Li4Ti5O12 (C-LTO) and carbon nanotube-Li4Ti5O12 (CNT-LTO) were synthesized by solvothermal method and subsequent high-temperature calcination. X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), and selected area electron diffraction (SAED) were applied to characterize the phase structure, particle morphology, and the coating structure. XRD analysis, TEM micrographs, HR-TEM images and SAED analysis revealed that both LTO particles exhibited a well-developed spinel nanocrystal structure with average sizes between 20-70 nm. The C-LTO particles exhibited roughly spherical shape coated by an amorphous carbon layer up to 10 nm in thickness. The CNT-LTO samples showed uniform square nanocrystals with edge length around 20 nm and nanoscale graphitic layers covering the surface, revealing the carbon nanotubes interconnection networks among the particle assemblies. Electrochemical studies of lithium insertion/extraction performance are evaluated by the galvanostatic charge/discharge tests, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). Both LTO particles showed the superior initial discharge capacity of more than 200 mAh/g at 1/10C rate. The irreversible capacity of the C-LTO particles at more cycles was due to large polarization resulted from excessive carbon and possible residual precursors. The CNT-LTO particles show larger reversible capacity and enhanced electrochemical Li+ insertion/extraction kinetics at different cycling rates. The comparative structural and electrochemical analyses demonstrated that both nanoscale graphitic covering layers and the CNT interconnection networks increase the electronic conductivity and improve the kinetics rates of lithium insertion/extraction in the CNT-LTO particles.

Preparation and Electrochemical Behavior of Li4 Ti5 O12 Nanosheets As Anode Material for Lithium Ion Battery

Preparation and electrochemical lithium storage of flower-like spinel Li4Ti5O12 consisting of nanosheets

Synthesis and Characterization of CaTi2O4 (OH)2 Nanosheets for Lithium-Ion Battery

Structure and Electrochemical Properties of Spinel Li4ti5o12 Nanocomposites As Anode for Lithium-Ion Battery

Hydrothermal synthesis of layered Li 1.81H 0.19Ti 2O 5·xH 2O nanosheets and their transformation to single-crystalline Li 4Ti 5O 12 nanosheets as the anode materials for Li-ion batteries

Nano-sized Li4Ti5O12 Anode Material with Excellent Performance Prepared by Solid State Reaction: the Effect of Precursor Size and Morphology

Facile Preparation of Nanocrystalline Li4Ti5O12 and Its High Electrochemical Performance As Anode Material for Lithium-Ion Batteries

Synthesis of sawtooth-like Li4Ti5O12 nanosheets as anode materials for Li-ion batteries

Preparation and Characterization of Li4Ti5O12 Anode Material for Lithium Secondary Batteries

Preparation Of Li4ti5o12 Nanorods As Anode Materials For Lithium-Ion Batteries

Facile Synthesis and Characterization of Li4Ti5O12 As Anode Material for Lithium Ion Batteries

Facile Synthesis Of Li4ti5o12 Nanosheets Stacked By Ultrathin Nanoflakes For High Performance Lithium Ion Batteries

Preparation of Li[sub 4]Ti[sub 5]O[sub 12] Nanorods as Anode Materials for Lithium-Ion Batteries

Mechanochemical Synthesis and Electrochemical Performances of Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub> Anode Materials for Lithium Ion Batteries

Synthesis of Li4Ti5O12 Nanostructural Anode Materials with High Charge–discharge Capability

Mechanochemical Synthesis and Electrochemical Performances of Li4Ti5O12 Anode Materials for Lithium Ion Batteries

Hydrothermal Synthesis of Li4Ti5O12/TiO2 Nano-composite As High Performance Anode Material for Li-Ion Batteries

Facile Synthesis of Nanocrystalline Li4Ti5O12 by Microemulsion and Its Application As Anode Material for Li-ion Batteries

VOPO4 Nanosheets As Anode Materials for Lithium-Ion Batteries.

Li4Ti5O12 anode materials applied in lithium ion batteries

Simple preparation of petal-like TiO 2 nanosheets as anode materials for lithium-ion batteries