Oxidation of Nitric Oxide on Gas-Phase Cerium Oxide Clusters via Reactant Adsorption and Product Desorption Processes.
F. Mafuné,Toshiaki Nagata,K. Miyajima
DOI: https://doi.org/10.1021/acs.jpca.5b07749
2015-09-30
Abstract:The reactivity of cerium oxide cluster cations, CenO2n+x(+) (n = 2-9, x = -1 to +2), with NO was investigated using gas-phase temperature-programmed desorption (TPD) combined with mass spectrometry. Target clusters were prepared in the gas phase via the laser ablation of a cerium oxide rod in the presence of oxygen, which was diluted using helium as a carrier gas. NO adsorbed onto stoichiometric and oxygen-rich clusters of CenO2n+x(+) (x = 0-2), forming CenO2n+x(NO)(+) (x = 0-2) species. Gas-phase TPD was measured for the NO-adsorbed clusters, revealing that CenO2n(NO)(+) released NO2 at 600-900 K, forming CenO2n-1(+). Therefore, the overall reaction was the oxidation of NO by the CenO2n(+) clusters, which was explained in terms of a Langmuir-Hinshelwood type reaction. An activation barrier existed between the initial complex (CenO2n(NO)(+)) and the final oxidation products (CenO2n-1(+) + NO2). To determine the nature of the intermediates and the activation barrier, TPD was also performed on CenO2n-1(NO2)(+), which had been prepared through the adsorption of NO2 on CenO2n-1(+) for comparison. The activation barrier was associated with the release of NO2 from the intermediate complex (CenO2n-1(+)-NO2 → CenO2n-1(+) + NO2) rather than the structural rearrangement that formed NO2 in the other intermediate complex (CenO2n(+)-NO → CenO2n-1(+)-NO2).
Materials Science,Medicine,Chemistry