Abstract:The use of coatings to protect metals from corrosion is currently a common practice. In this study, a double bond-terminated waterborne polyurethane prepolymer was firstly synthesized from polycaprolactone polyol, toluene diisocyanate, dimethylolpropionic acid and hydroxyethyl methacrylate. Then, waterborne polyurethane prepolymer was modified with styrene, butyl acrylate, glycidyl methacrylate, and dodecafluoroheptyl methacrylate though soap-free emulsion polymerization method in order to obtain the crosslinked fluorinated acrylate modified waterborne polyurethane (CFWPUA). The CFWPUA emulsion was used as the matrix resin to prepare the coating with a bar coater, which possesses the characteristics of external hydrophobic surface constructed by long fluorinated side-chains and internal double cross-linking system. The results of infrared spectrum analysis proved the successful synthesis of modified waterborne polyurethane. The energy-dispersive X-ray spectroscopy results showed that the long fluorine side-chains partially migrate to the surface of the coating during the curing process, which leads to the occurrence of fluorine enrichment on the surface. When the glycidyl methacrylate content is 5 wt% and the dodecafluoroheptyl methacrylate content is 7.5 wt%, the water absorption rate of the membrane reduces to 7.9%, the water contact angle of the coating reaches 102.5°, and the gel content is 91%, which proved the successful construction of the double cross-linking system and prevents the penetration of water molecules. The pencil hardness of CFWPUA coating can reach 3H and flexibility and adhesion properties are at the highest level. Most importantly, in the electrochemical impedance spectroscopy test, the modified waterborne polyurethane coating effectively protects Q235 metal substrate from corrosion in the 3.5 wt% NaCl solution, the impedance modulus of CFWPUA coating could be maintained at about 107 Ω·cm2 for a long time, the resistance of CFWPUA coating slowly decreased from 2.124 × 107 Ω·cm2 to 9.605 × 106 Ω·cm2 within 10 days of immersion, two-time constant was generated after 12 days of immersion, which is slightly superior compare to commercial waterborne fluorocarbon coating. The modified waterborne polyurethane coating prepared here shows a potential practical application in the field of metal anti-corrosion.

Preparation and Application of Cationic Waterborne Polyurethane Modified by Perfluoroalkyl Side Chain

Preparation and Characterization of Fluorinated Acrylate and Epoxy Co-Modified Waterborne Polyurethane

Synthesis and Properties of Cationic Core-Shell Fluorinated Polyurethane Acrylate

Preparation and characterization of hydrophobic waterborne polyurethane self‐matting coating

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Influence of fluorine‐containing side chain on the properties of waterborne polyurethane‐urea

Preparation and properties of a novel waterborne fluorinated polyurethane–acrylate hybrid emulsion modified by long aliphatic chains

Effect of fluorine atom positions on the properties of waterborne polyurethanes

Emulsion homopolymerization of chlorotrifluoroethylene toward new waterborne fluorocarbon coatings

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Preparation and properties of waterborne polyurethane modified by aminoethylaminopropyl polydimethylsiloxane for fluorine-free water repellents

Study on the preparation and performance of perfluoroalkyl waterborne polyurethane-polyacrylate paper oil-resistant agent

Study of a Novel Fluorine-Containing Polyether Waterborne Polyurethane with POSS as a Cross-Linking Agent

Synthesis Of Fluoroalkyl-Modified Polyester And Its Application In Improving The Hydrophobicity And Oleophobicity Of Cured Polyester Coatings

Synthesis and properties of castor oil–based cationic waterborne polyurethane modified by epoxy resin

Environmentally friendly plant‐based waterborne polyurethane for hydrophobic and heat‐resistant films

Preparation and characteristics of crosslinked fluorinated acrylate modified waterborne polyurethane for metal protection coating

Facile hydrophobic modification of hybrid poly(urethane-urea)methacrylate aqueous dispersions and films through blending with novel waterborne fluorinated acrylic copolymers

Preparation and characterization of high solid content cationic waterborne polyurethane with core‐shell structures

Preparation and application of fluorine-containing acrylate emulsion in two-component waterborne polyurethane coatings

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates