Preparation of Novel Glass Phosphors by Spark Plasma Sintering

ZHANG Yan,JIANG You

DOI: https://doi.org/10.3969/j.issn.1000-2871.2013.06.002

2013-01-01

Abstract:Using laboratory-made SiO2 powder and commercial Ce ∶ YAG phosphor powder as raw materials,Ce: YAG quartz glass phosphors for high-power white LED have been successfully prepared through spark plasma sintering( SPS) at 1 200℃,50 MPa for 2 min. The as-prepared Ce∶ YAG glass phosphors were examined by XRD,photoluminescence spectrum and so on. The results showed that the crystal structure of Ce∶YAG phosphors was not destroyed after sintering and glassy phase was still the major phase in glass phosphor. It has a strong absorption around 460 nm and a broad emission band peaked at 530 nm excited by 460 nm at room temperature. The research results indicate that the Ce∶YAG glass phosphor can be a novel promising phosphor for packing material of high-power white LED.