Rapid-preparation and characteristics of magnesium hydroxide nanoparticles with high dispersibility

Li Zhenzhong,He Wei,Liu Jingbing,Zhang Wenxiong

DOI: https://doi.org/10.3969/j.issn.1006-4990.2007.11.007

2007-01-01

Abstract:Flaky magnesium hydroxide(MH) nanoparticles with high dispersibility were rapidly prepared by high temperature precipitation-hydrothermal method with magnesium chloride as raw material and ammonia as precipitator.The topography and crystal structure of MH nanoparticles were characterized by SEM and XRD.Meanwhile,the MH nanoparticles were filled into the Ethylene Vinyl Acetate(EVA)resin.The torque rheological,mechanical and fire resistant properties of EVA/MH mixture were studied by torque rheometer,tension tester and oxygen index tester.The results showed that the obtained MH product was hexagonal slice with high dispersibility,good filterability and great compatibility with EVA(which become better while increasing the hydrothermal duration).When the filling amount of MH was 50%(mass fraction),the EVA/MH mixture had excellent rheological and mechanical properties with balance torque of 17 N·m,tensile strength of 10.9 MPa and elongation at break of 470%.