Tribological Properties of γ-ray Irradiation Cross-linked Ultra High Molecular Weight Polyethylene

HUANG Chuan-hui,LIU Qing-hua,ZHANG Lei,WANG Qing-liang

DOI: https://doi.org/10.3969/j.issn.1674-358X.2010.03.001

2010-01-01

Abstract:Different doses ofγ-ray were used to irradiate on UHMWPE surface and prepare the irradiation cross-linking UHMWPE materials.The crystallinity and surface hardness were measured by XRD and ball indentation hardness test.The friction and wear tests of untreated and irradiated UHMWPE samples were carried out on a universal micro-tribometer(UMT-II)under the lubrication condition of 25%bovine serum solution.The experimental results show that the crystallinity and surface hardness of irradiation cross-linking UHMWPE increases with increasing doses ofγ-ray,and both of them have the same variation.All irradiation cross-linking samples have the lower wear rates and high wear resistance.But the coefficients of friction of are higher than the untreated one.The wear mechanisms of un-irradiated UHM-WPE are dominated by adhesive wear and plastic deformation.The treated samples are characterized by fatigue and abrasive wears.