MICROSTRUCTURE OF THE LATEX PREPARED THROUGH AQUEOUS TWO-PHASE POLYMERIZATION OF ACRYLAMIDE IN AQUEOUS POLY(ETHYLENE GLYCOL) SOLUTION
Lue Ting,Shan Guorong,Shang Kuanxiang
DOI: https://doi.org/10.3724/sp.j.1105.2010.09203
2010-01-01
Acta Polymerica Sinica
Abstract:A latex of poly(acrylamide)(PAM) dispersed in a aqueous solution was successfully prepared through aqueous two-phase polymerization of acrylamide(AM) in aqueous poly(ethylene glycol)(PEG) solution with 2,2'-azobis[2-(2-imidazolin-2-yl) propane ]-dihydrochloride(VA044) as the initiator.The effects of initiator,monomer and PEG concentrations,as well as the temperature,on the morphology and size of the droplets rich in PAM were systemically investigated.High initiator concentration leads to a high rate of polymer chains aggregation,which causes the small droplets separate from the continuous phase rapidly.The low viscosity in the earlier stage of polymerization could not prevent the coalescence of small droplets.At the same time,the high internal viscosity of the droplets is great enough to prevent easy diffusion of molecules between the coalescing droplets.Therefore,stripe shape droplets were generated.Since more monomer was consumed to generate small droplets because of high initial initiator concentration,less monomer polymerized inside the droplets.Thus,the stripe shape droplets can not become plump.The popcorn shape droplet was formed due to the aggregation between bigger droplets and small droplets.With temperature rising from 30℃ to 52.5℃,the rate of initiator decomposition accelerated,and the critical chain length of PAM separated from continuous phase shortened,both of which make the droplet morphology trend to stripe shape.However,monomer partition coefficient decreased with temperature rising meaning that more polymerization occurred inside droplets and the droplets formation was slowed.The former factor was inclined to form stripe shape droplets,and the latter trended to generate spherical droplets.Thus,the droplet shifted from round shape to stripe shape,and then formed round shape again.At low initial monomer concentration,the polymerization was very slow.However,higher monomer concentration causes the small droplets separate rapidly from continuous phase which leads to the small droplets aggregate easily at early stage of the polymerization.The aggregation of the droplets was strained with increasing viscosity of the continuous phase with the development of the polymerization.Small droplets started to exist stably in aqueous PEG solution.Thus,the droplets size distribution became wide.The increase of PEG concentration reduced the coalescence of the droplets,and also decreased the monomer partition coefficient,both of which made the droplets shifted from stripe shape to round shape.However,the increasing PEG concentration decreased the critical chain length which would form more droplets.As a result,the droplet size increased indistinctly.